| 牌号简介 About |
|---|
| Vydyne®65B（干燥）Vydyne 65B是一种中等粘度的PA66树脂，适用于注塑，挤出和复合应用。它只有自然色。泛达65B树脂具有高强度，刚性和韧性，适用于各种苛刻的应用，并且对各种化学品，溶剂和油具有良好的流体阻力。典型应用/最终用途：典型用途包括包装薄膜，单丝，刷毛，棒材，管材和片材。＆Vydyne®65BVydyne 65B是一种用于挤出复合的中高粘度树脂。希望将这种纯树脂包括在配方中，其中最终产品的熔体强度对于应用是关键的。泛达65B具有良好的初始颜色，其水分含量低于0.1％。泛达65B耐热，耐油和耐磨是PA66纯树脂的典型特征。 Vydyne® 65B (Dry) Vydyne 65B is a medium-viscosity PA66 resin suitable for injection-molding, extrusion and compounding applications. It is available in natural color only. Vydyne 65B resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Vydyne® 65B Vydyne 65B is a medium-high-viscosity resin used for extrusion-compounding. It is desirable to include this neat resin in a formulation in which the melt strength of the final product is critical for the application. Vydyne 65B exhibits good initial color and it has a moisture level below 0.1%. Resistance of Vydyne 65B to heat, oil and wear is typical of PA66 neat resins. |
产品描述 Product Description
用途：片材;棒材;工业应用;通用;型材;单丝;复合;管件;
颜色：自然色,自然色
加工条件：挤出 Extrusion
性能特点： 机械强度好; 耐油; 耐汽油; 耐化学性; 颜色稳定; 韧性好; Good Rigidity,Good flexibility,Good color stability,Grease resistance,Solvent resistance,Gasoline resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.14 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD：23℃，2.0 mm TD：23℃，2.0 mm |
1.9 | % | ISO 294-4 |
|
MD：23℃，2.0 mm MD：23℃，2.0 mm |
2.0 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
8.5 | % | ISO 62 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
2.5 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服，23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
|
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
|
23℃ 23℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
泊松比 Poisson's ratio |
ISO 527-2 | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~55℃，2 mm TD：23~55℃，2 mm |
1/℃ | ISO 11359-2 | |
|
MD：23~55℃，2 mm MD：23~55℃，2 mm |
1/℃ | ISO 11359-2 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Formic acid |
|
【新闻资讯】查看全部 
日本4月化学品出口增长28.5%
2021-05-21 搜料网资讯： 据ICIS网站5月20日报道 周四公布的官方数据显示，日本4月份化学品出口同比增长28.5%，至9550亿日元（88亿美元），支撑了海外出货量的整体增长。 日本经济产业省（METI）在 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付