| 牌号简介 About |
|---|
| Vydyne® 75HF是专为挤出应用而设计的中高粘度热稳定PA66/6共聚物树脂。本产品仅限天然产品。具有熔点高、强度高、刚性好、韧性好、手感柔软、耐化学性好等特点，是工程性能的平衡组合。这种树脂特别适用于需要高延伸率、薄截面清晰度和柔软手感的应用。典型应用/最终用途：典型用途包括包装膜、单丝、刚毛和挤压型材。 Vydyne 75HF is a medium-high-viscosity, heat-stabilized PA66/6 copolymer resin designed for extrusion applications. This product is available in natural only. It offers a well-balanced combination of engineering properties characterized by high melt point; high strength and rigidity; good toughness; soft hand and good chemical resistance. |
产品描述 Product Description
用途：薄膜;片材;棒材;工业应用;型材;单丝;真空袋薄膜;管件;
颜色：自然色
加工条件：挤出 Extrusion
性能特点： 热稳定性好; 机械强度好; 熔体稳定性高; 耐油; 耐汽油; 耐化学性; 高分子量; 韧性好; Good Rigidity,Good flexibility,High molecular weight,Grease resistance,Solvent resistance,Gasoline resistance,Heat Stabilized,Higher melt stability
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.14 | g/cm³ | ISO 1183 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
8.5 | % | ISO 62 |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
2.5 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
2700 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
断裂，23℃ Fracture, 23 ℃ |
50.0 | MPa | ISO 527-2 |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
|
TD，断裂，吹塑薄膜 TD, fracture, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，吹塑薄膜 MD, fracture, blow molded film |
MPa | ASTM D882 | |
|
Ultimate Ultimate 2 |
MPa | ASTM D882 | |
|
Ultimate Ultimate 3 |
MPa | ASTM D882 | |
|
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
|
23℃ 23℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
泊松比 Poisson's ratio |
ISO 527-2 | ||
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus |
|||
|
1% 正割，TD，铸造薄膜 1% secant, TD, cast thin film |
MPa | ASTM D882 | |
|
1% 正割，MD，铸造薄膜 1% secant, MD, cast thin film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
|||
|
屈服，23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
|
TD，断裂，铸造薄膜 TD, fracture, cast thin film |
% | ASTM D882 | |
|
TD，屈服，铸造薄膜 TD, yield, cast thin film |
% | ASTM D882 | |
|
MD，断裂，挤塑薄膜 MD, fracture, extruded film |
% | ASTM D882 | |
|
MD，屈服，铸造薄膜 MD, yield, cast thin film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 4 |
|||
|
42 µm，铸造薄膜 42 µ m, cast thin film 4 |
g | ASTM D1709 | |
|
撕裂强度 tear strength |
|||
|
TD，42 µm，铸造薄膜 TD, 42 µ m, cast thin film |
g | ASTM D1922 | |
|
MD，42 µm，铸造薄膜 MD, 42 µ m, cast thin film |
g | ASTM D1922 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：23~55℃，2 mm TD：23~55℃，2 mm |
1/℃ | ISO 11359-2 | |
|
MD：23~55℃，2 mm MD：23~55℃，2 mm |
1/℃ | ISO 11359-2 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 (TD) |
| 3 (MD) |
| 4 (f50) |
|
【新闻资讯】查看全部 
Toyota Racing采用聚酰胺材料3D打印赛车部件
2022-06-13 Stratasys是一家聚合物3D打印技术公司，目前是 Toyota Racing Development (TRD)的官方合作伙伴。该合作关系将在即将到来的GR Cup丰田GR86上首次亮相，3D打印生产部件是SRO America批准的新单品牌赛 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |