牌号简介 About |
---|
KetaSpire KT- 880 GF20是高流动性 、20 %玻纤增强聚醚醚酮( PEEK)。强度和刚度高于未增强KetaSpire PEEK树脂。玻纤增强同时赋予材料在结构性产品中更高的机械强度,尤其是工作温度接近300℃的条件下。 KetaSpire PEEK按照行业最高标准加工,以兼具各种出色的性能为特征,包括优异的耐磨损性、一流的抗疲劳性、易于熔融加工、高纯度、优异的耐有机物、酸和碱等化学物质的性能。 这些特性使得它非常适合医疗保健、交通运输、电子、化学处理和其它工业用途。 KetaSpire® KT-880 GF20 is a high flow, 20% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. The glass fiber content is optimized to provide a balance of strength and stiffness with toughness-related properties, such as impact resistance and elongation at break. This level of reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 240°C (464°F). KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
60 | kJ/m² | ISO 179 |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
60 | J/m | ASTM D256 |
-- -- |
6.0 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
770 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
345 | ℃ | ISO 11357 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弹性模量 Elastic modulus |
|||
-- -- |
GPa | ISO 527 | |
-- -- |
GPa | ASTM D638 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ISO 15512 | |
灰份含量 Ash Content |
% | ISO 3451-1 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 DSC First heat |
【新闻资讯】查看全部
扬子石化低温乙烯装置停车大修全面启动
2016-10-31 经过4天的工艺处理,10月24日,扬子石化低温乙烯装置各系统容器、设备退料、系统吹扫等工作逐步结束,储罐液相乙烯全部彻底倒空,标志着低温乙烯装置停车大修全面启动。 目前,各参战施工单位陆续进入现场,装置设备检修、大修改造等项目提前进行交底,计划在45天的工期内,完成全系统30个项目的大修任务,让老设备焕发新生,为装置下一轮运行提质增效 添后劲。 低温乙烯贮存装置自1995年建成投产,是当时该类装置在祖国大陆地区首套装置,因此储存低温乙烯的T01贮罐被誉为“华 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |