PEEK，KetaSpire® KT-880 GF20对比PEEK，ZYPEEK®330GL30H物性表,价格行情_搜料

牌号信息	KetaSpire® KT-880 GF20 物性表 PEEK & 比利时索尔维指导价格：暂无塑料库存：缺货	ZYPEEK®330GL30H 物性表 PEEK & 吉林中研指导价格：暂无塑料库存：缺货
牌号简介	KetaSpire KT- 880 GF20是高流动性、20 ％玻纤增强聚醚醚酮（ PEEK）。强度和刚度高于未增强KetaSpire PEEK树脂。玻纤增强同时赋予材料在结构性产品中更高的机械强度，尤其是工作温度接近300℃的条件下。 KetaSpire PEEK按照行业最高标准加工，以兼具各种出色的性能为特征，包括优异的耐磨损性、一流的抗疲劳性、易于熔融加工、高纯度、优异的耐有机物、酸和碱等化学物质的性能。这些特性使得它非常适合医疗保健、交通运输、电子、化学处理和其它工业用途。 KetaSpire® KT-880 GF20 is a high flow, 20% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. The glass fiber content is optimized to provide a balance of strength and stiffness with toughness-related properties, such as impact resistance and elongation at break. This level of reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 240°C (464°F). KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.

产品描述
厂家：	比利时索尔维 Solvay	吉林中研 ZYPEEK
类别：	PEEK	PEEK PEEK
填料：	玻璃纤维 30	玻璃纤维 30
用途：	密封件,外科器械,薄膜,电气/电子应用领域,连接器,石油/天然气用品,工业应用,泵件,飞机应用,牙齿应用领域,医疗器械,医疗器材,汽车领域的应用,医疗/护理用品
性能特点：	蒸汽消毒,耐蒸汽,抗伽马射线,易消毒,尺寸稳定性好,加热消毒,耐疲劳性好,环氧乙烷消毒,放射线可穿透,辐射消毒,耐化学性,生物兼容性,阻燃,电子束消毒,机械强度好,高压灭菌器消毒,耐高温,流动性高 Steam sterilized,Resistance to the steam,Gamma radiation,Good disinfection,Good Dimensional Stability,Heat sterilization,Fatigue resistance,Ethylene oxide disinfection,Radioactive,Radiation disinfection,Solvent resistance,Biocompatible,Flame Characteristics,E-beam disinfection,Good Rigidity,High pressure disinfection,High Heat Resistance,High liquidity
加工条件：	注射成型 Injection Molding

技术参数

冲击性能
IMPACT KetaSpire® KT-880 GF20 ZYPEEK®330GL30H 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam kJ/m² ISO 180/U

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180/A

悬臂梁缺口冲击强度(--)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(--)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179-1eA

热性能
THERMAL KetaSpire® KT-880 GF20 ZYPEEK®330GL30H 单位
UNIT 测试方法
TEST METHOD

Tg(起始)
Tg (starting) ℃ ISO 11357

比热容(23℃)
Specific heat capacity kJ/kg /℃ DSC

热变形温度(1.8 Mpa)
Hot deformation temperature ℃ ISO 75-f

热导系数(23℃)
Thermal conductivity coefficient W/m/K ISO 22007-4

熔点
melting point ℃ ISO 11357

熔融温度
Melting temperature ℃ ISO 11357

线性热膨胀系数(低于Tg沿着流动方向)
Linear coefficient of thermal expansion ppm/K ISO 11359

线性热膨胀系数(高于Tg沿着流动方向)
Linear coefficient of thermal expansion ppm/K ISO 11359

电气性能
ELECTRICAL KetaSpire® KT-880 GF20 ZYPEEK®330GL30H 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant ASTM D150

介电常数(1 MHz)
Dielectric constant ASTM D150

介电常数(23 ℃, 1 kHz)
Dielectric constant IEC 60250

介电常数(60 Hz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

介电强度(2 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率(23 ℃，1V)
Volume resistivity ohms·cm IEC 60093

体积电阻率(275 ℃)
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 kHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor ASTM D150

耗散因数(23℃，1 MHz)
Dissipation factor IEC 60250

耗散因数(60 Hz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms ASTM D257

机械性能
MECHANICAL KetaSpire® KT-880 GF20 ZYPEEK®330GL30H 单位
UNIT 测试方法
TEST METHOD

压缩强度(23℃)
compressive strength MPa ISO 604

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(断裂，23℃)
bending strength MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

弹性模量(--)
Elastic modulus GPa ASTM D638

弹性模量(--)
Elastic modulus GPa ISO 527

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂，23℃)
Tensile strain % ISO 527

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-2

洛氏硬度(M 级)
Rockwell hardness ASTM D785

邵氏硬度(23℃)
Shore hardness D 级 ISO 868

物理性能
PHYSICAL KetaSpire® KT-880 GF20 ZYPEEK®330GL30H 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr，3.2 mm厚拉伸棒)
Water absorption rate % ISO 62-1

吸水率(24hr)
Water absorption rate % ISO 15512

吸水率(平衡，23℃)
Water absorption rate % ISO 62-1

密度
Density g/cm³ ISO 1183

密度(结晶)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 294-4

灰份含量
Ash Content % ISO 3451-1

熔体表观粘度(400℃，1000 sec^-1)
Apparent viscosity of melt Pa·s ASTM D3835

熔体质量流动速率(380℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(400℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

加工方式

注射 KetaSpire® KT-880 GF20 ZYPEEK®330GL30H 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度 KetaSpire® KT-880 GF20 ZYPEEK®330GL30H 单位测试方法

螺杆压缩比

备注

1 一般属性：这些不能被视为规格。

2 DSC First heat


相关资讯

牌号简介
产品描述
技术参数
冲击性能
热性能
电气性能
机械性能
物理性能
加工方式
注射
注射速度
备注
返回顶部

PEEK，KetaSpire® KT-880 GF20对比PEEK，ZYPEEK®330GL30H对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别