牌号简介 About |
---|
Lexan Exl4019树脂Lexan Exl4019是一种不透明的9%玻璃纤维(GF)增强聚碳酸酯(PC)硅氧烷共聚物树脂,用于注塑成型(IM)应用,需要提高刚度。与标准PC相比,该树脂还比传统的GF增强PC树脂具有更好的延展性,同时具有中等的流动特性和良好的加工性能,有机会缩短IM循环时间。LEXAN™ EXL4019 resin是一种产品,可能是多种应用的最佳候选产品。仅限有限颜色。 LEXAN EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers improved ductility over conventional GF reinforced PC resins in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times when compared to standard PC. LEXAN EXL4019 resin is a product that may be an excellent candidate for a wide variety of applications. Available in limited colors only. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
颜色:可用颜色,不透明
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 机械强度好; 成型周期快; 共聚物; 流动性中等; 机械强度好-延展; 易加工; Good Rigidity,Excellent Processability,Ductility,Quick molding cycle,Moderate liquidity,Copolymer,HB
填料:玻璃纤维 9
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
密度 Density |
1.25 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
7.5 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
6.50 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.20 to 0.60 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 9 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
75℃ 75℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 120*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
研讨人员开发了自修复塑料、凝胶或弹性体
2018-09-06 自修复聚合物材料作为一种智能材料,可以修复在使用过程中因外力作用而产生的裂纹或局部损伤,从而恢复其原有的功能,延长其使用寿命。该材料在表面镀层保护、生物医药材料、锂电池以及航空航天等领域具有潜在的应用前景。为了满足不同的应用,研究人员将“牺牲键”引入到聚合物材料中,开发了自修复塑料、凝胶或弹性体。对于自修复弹性体材料来说,兼顾良好的机械性能、高效的自修复效率及优异的光学性能是一个挑战性难题。 在国家自然科学基金委的支持下,中国科学院化学研究所工程塑料重点实验室研究员董侠等致力于智能材料的开 |
研讨人员开发了自修复塑料、凝胶或弹性体 自修复聚合物材料作为一种智能材料,可以修复在使用过程中因外力作用而产生的裂纹或局部损伤,从而恢复其原有的功能,延长其使用寿命。该材料在表面镀层保护、生物医药材料、锂电池以及航空航天等领域具有潜在的应用前景。为了满足不同的应用,研究人员将“牺牲键”引入到聚合物材料中,开发了自修复塑料、凝胶或弹性体。对于自修复弹性体材料来说,兼顾良好的机械性能、高效的自修复效率及优异的光学性能是一个挑战性难题。 在国家自然科学基金委的支持下,中国科学院化学研究所工程塑料重点实验室研究员董侠等致力于智能材料的开发与应用,取得了系列进展。在此基础上,从分子设计角度出发,提出了一种新型自修复设计策略“Phase Locked Dynamic Chemical Bonds(相锁定动态化学键)”,成功制备出无色透明、可快速自修复的高韧高强聚合物。 研究工作通过“硬段锁定”和“微相分离控制”相结合的策略展开,设计的含二硫键自愈聚氨酯弹性体(PUDS)呈现出无色透明的优异光学性质,最大拉伸强度可达25 MPa,断裂伸长率超过1600%,在温和加热条件下(70oC),弹性体表面划痕可在60s内迅速恢复,同时表现出良好的重复刮擦自修复功能,经多次刮擦自修复后材料的雾度值仅为0.6%。这种无色高透明的自修复特征,使得该材料在光学领域具有重要的应用前景。相关成果发表于《先进材料》。 来源:中国科学院 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 工地安全帽
- 2019-08-21 0
- Lexan Exl4019树脂Lexan Exl4019是一种不透明的9%玻璃纤维(GF)增强聚碳酸酯(PC)硅氧烷共聚物树脂,用于注塑成型(IM)应用,需要提高刚度。与标准PC相比,该树脂还比传统的GF增强PC树脂具有更好的延展性,同时具有中等的流动特性和良好的加工性能,有机会缩短IM循环时间。LEXAN™ EXL4019 resin是一种产品,可能是多种应用的最佳候选产品。仅限有限颜色。
- 阅读全文
工地安全帽
收起
抱歉!暂无数据。