PC，LEXAN™ EXL4019 resin对比PC，LEXAN™ ML7667 resin物性表,价格行情_搜料

牌号信息	LEXAN™ EXL4019 resin 物性表 PC & 沙特沙伯基础指导价格：28875.0元/吨塑料库存： 26750kg	LEXAN™ ML7667 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Lexan Exl4019树脂Lexan Exl4019是一种不透明的9%玻璃纤维（GF）增强聚碳酸酯（PC）硅氧烷共聚物树脂，用于注塑成型（IM）应用，需要提高刚度。与标准PC相比，该树脂还比传统的GF增强PC树脂具有更好的延展性，同时具有中等的流动特性和良好的加工性能，有机会缩短IM循环时间。LEXAN™ EXL4019 resin是一种产品，可能是多种应用的最佳候选产品。仅限有限颜色。 LEXAN EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers improved ductility over conventional GF reinforced PC resins in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times when compared to standard PC. LEXAN EXL4019 resin is a product that may be an excellent candidate for a wide variety of applications. Available in limited colors only.	Lexan ML7667树脂Lexan ML7667专用聚碳酸酯（PC）树脂是一种9%玻璃纤维增强，紫外线稳定，阻燃注射成型等级。该中流量专用PC树脂将UL94V0@1.5mm、5VB@3.0mm阻燃剂与无氯、无溴阻燃剂相结合，具有优良的加工性能、改善的释放性能和良好的冲击性能。本产品仅提供有限的不透明颜色，可能是广泛应用的理想选择，即电气和电子外壳应用。 LEXAN ML7667 specialty polycarbonate (PC) resin is a 9% GF reinforced, UV stabilized, flame retarded injection molding grade. This medium flow specialty PC resin combines UL94 V0 @ 1.5mm, 5VB @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR agents with excellent processability, improved release performance and good impact performance. This product is available in limited opaque colors only and may be an excellent candidate for a broad range of applications, i.e. electrical and electronic enclosure applications.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	玻璃纤维 9	玻璃纤维 9
用途：		电气/电子应用领域,电器外壳
性能特点：	机械强度好,易加工,机械强度好-延展,成型周期快,流动性中等,共聚物,防火阻燃等级HB Good Rigidity,Excellent Processability,Ductility,Quick molding cycle,Moderate liquidity,Copolymer,HB	耐候抗UV,易加工,冲击性能好,无卤,含脱模剂,阻燃,防火阻燃等级HB,防火阻燃等级V-0,防火阻燃等级5VB Weather resistance is good,Excellent Processability,High impact resistance,Halogen free,Good stripping performance,Flame Characteristics,HB,V-0,5VB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ EXL4019 resin LEXAN™ ML7667 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LEXAN™ EXL4019 resin LEXAN™ ML7667 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ EXL4019 resin LEXAN™ ML7667 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ EXL4019 resin LEXAN™ ML7667 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(125℃)
Ball pressure test IEC 60695-10-2

球压测试(75℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY LEXAN™ EXL4019 resin LEXAN™ ML7667 resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.1 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(2.5 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

电气性能
ELECTRICAL LEXAN™ EXL4019 resin LEXAN™ ML7667 resin 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数
Compared to the leakage tracing index UL 746

加工方式

注射 LEXAN™ EXL4019 resin LEXAN™ ML7667 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*3

9 120*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)