| 牌号简介 About |
|---|
| Lexan Exl4019树脂Lexan Exl4019是一种不透明的9%玻璃纤维（GF）增强聚碳酸酯（PC）硅氧烷共聚物树脂，用于注塑成型（IM）应用，需要提高刚度。与标准PC相比，该树脂还比传统的GF增强PC树脂具有更好的延展性，同时具有中等的流动特性和良好的加工性能，有机会缩短IM循环时间。LEXAN™ EXL4019 resin是一种产品，可能是多种应用的最佳候选产品。仅限有限颜色。 LEXAN EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers improved ductility over conventional GF reinforced PC resins in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times when compared to standard PC. LEXAN EXL4019 resin is a product that may be an excellent candidate for a wide variety of applications. Available in limited colors only. |
产品描述 Product Description
颜色：可用颜色,不透明
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 机械强度好; 成型周期快; 共聚物; 流动性中等; 机械强度好-延展; 易加工; Good Rigidity,Excellent Processability,Ductility,Quick molding cycle,Moderate liquidity,Copolymer,HB
填料：玻璃纤维 9
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.25 | g/cm³ | ASTM D792 |
|
密度 Density |
1.25 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
7.5 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
6.50 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
TD：3.2 mm TD：3.2 mm |
0.20 to 0.60 | % | 内部方法 |
|
MD：3.2 mm MD：3.2 mm |
% | 内部方法 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/5 | |
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/5 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/5 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
|
-30℃ -30℃ |
ISO 180/1U | ||
|
23℃ 23℃ |
ISO 180/1U | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 9 |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Ae | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
75℃ 75℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
0.75 mm 0.75 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.20 in/min |
| 3 类型 1, 0.20 in/min |
| 4 0.051 in/min |
| 5 0.079 in/min |
| 6 Yield |
| 7 80*10*3 sp=62mm |
| 8 80*10*3 |
| 9 120*10*4 mm |
| 10 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
轻，弹，耐用且透气！东洋纺为日本一艘新船提供座椅弹性材料
2022-11-21 扫描上图二维码，可以免费下载 搜料 APP 近日，纤维和纺织品制造商东洋纺株式会社（Toyobo）宣布，正在为一艘新下水的日本船舶的座椅提供一种三维结构弹性纤维材料。 Aoi船上的头等 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付