牌号简介 About |
---|
高密度聚乙烯超高分子量,己烯共聚物挤出吹塑的特点KPOL HD K-10.0/948,是一种高分子量高密度聚乙烯,共聚物。具有良好的加工性能、优异的抗应力开裂性能(ESCR)、优异的刚度和冲击强度。适用于大批量吹塑。典型的吹塑应用包括20到200升的容器和圆桶,用于化工、农用化学品和食品包装,小罐和床衬垫,托盘,汽车衬垫,卡车床衬垫。KPOL树脂符合第21章第177.1520节第c段的要求,命名为“烯烃聚合物”,来自FDA联邦法规,用于直接食品接触。 High Density Polyethylene Extra high molecular weight, hexene copolymer Extrusion-Blow Molding Characteristics The KPOL HD K-10.0/948, is a high molecular weight high-density polyethylene, copolymer. Offers good processability, outstanding stress cracking resistance (ESCR), excellent stiffness and impact strength. Suitable for blow molding of large volumes. Applications Typical blow molded applications include containers and drums from 20 to 200 liters, for chemical, agrochemical and food package, small tanks and bedliner, Pallets, Automotive dunnage, Truck bedliners. The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.948 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
10 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,1.91 mm,10%润湿剂 50 ℃, 1.91 mm, 10% wetting agent |
200 | hr | ASTM D1693B |
50 ℃,3.18 mm,100%润湿剂 50 ℃, 3.18 mm, 100% wetting agent |
> 650 | hr | ASTM D1693A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength |
195 | kJ/m² | ASTM D1822 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | DSC | |
热变形温度 Hot deformation temperature |
℃ | ASTM D648 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
正切 tangent |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |