HMW-HDPE，KPOL-HDPE HD K-10.0/948对比HMW-HDPE，Marlex® HXM 50100物性表,价格行情_搜料

牌号信息	KPOL-HDPE HD K-10.0/948 物性表 HMW-HDPE & 美国KPOL 指导价格：暂无塑料库存：缺货	Marlex® HXM 50100 物性表 HMW-HDPE & 沙特Saudi 指导价格：暂无塑料库存：缺货
牌号简介	高密度聚乙烯超高分子量，己烯共聚物挤出吹塑的特点KPOL HD K-10.0/948，是一种高分子量高密度聚乙烯，共聚物。具有良好的加工性能、优异的抗应力开裂性能（ESCR）、优异的刚度和冲击强度。适用于大批量吹塑。典型的吹塑应用包括20到200升的容器和圆桶，用于化工、农用化学品和食品包装，小罐和床衬垫，托盘，汽车衬垫，卡车床衬垫。KPOL树脂符合第21章第177.1520节第c段的要求，命名为“烯烃聚合物”，来自FDA联邦法规，用于直接食品接触。 High Density Polyethylene Extra high molecular weight, hexene copolymer Extrusion-Blow Molding Characteristics The KPOL HD K-10.0/948, is a high molecular weight high-density polyethylene, copolymer. Offers good processability, outstanding stress cracking resistance (ESCR), excellent stiffness and impact strength. Suitable for blow molding of large volumes. Applications Typical blow molded applications include containers and drums from 20 to 200 liters, for chemical, agrochemical and food package, small tanks and bedliner, Pallets, Automotive dunnage, Truck bedliners. The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.	Marlex® HXM 50100是一种高密度 (HMW) 聚乙烯材料,。该产品在北美洲、拉丁美洲或欧洲有供货,加工方式为:吹塑成型、挤出或热成型。 Marlex® HXM 50100的主要特性有: 阻燃/额定火焰高分子量高抗环境应力断裂能力 (ESCR) 己烯共聚单体坚硬典型应用领域包括: 汽车行业容器罐子包袋/内衬工程/工业配件 This extra high molecular weight, ethylene-hexene copolymer is tailored for large blow molded and thermoformed parts that require: Good melt strength Good rigidity Excellent ESCR Excellent low temperature impact strength Durability Recyclability Typical blow molded applications for HXM 50100 include: Shipping containers Jerry cans Fuel containers Agricultural chemical tanks Typical thermoformed applications for HXM 50100 include: Pallets Automotive dunnage Truck bedliners Playground equipment This resin meets these specifications: ASTM D4976 - PE 235 FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per Table 2 of 21 CFR 176.170(c) UL94HB yellow card per UL file E54700 NSF Standard 61 for potable water Listed in the Drug Master File

产品描述
厂家：	美国KPOL	沙特Saudi
类别：	HMW-HDPE HMW-HDPE	HMW-HDPE HMW-HDPE
填料：
用途：	托盘,食品包装,汽车领域的应用,鼓,农业应用,容器	托盘,容器,农业应用,衬里,油箱,户外家具,农用水箱,装运容器,汽车领域的应用,吹制容器
性能特点：	机械强度好,易加工,冲击性能好,食品接触,抗氧化,高分子量,共聚物,高密度,抗应力开裂 Good Rigidity,Excellent Processability,High impact resistance,Food contact compliance,Inoxidizability,High molecular weight,Copolymer,High density,High ESCR	食品接触,熔体强度好,超高分子量,经久耐用,耐低温冲击,己烯共聚单体,抗应力开裂,防火阻燃等级HB Food contact compliance,Good melt strength,Ultra high molecular weight,Durability,low-temperature impact resistance,Hexene copolymers,High ESCR,HB
加工条件：	吹塑成型	热成型 Thermo forming

技术参数

物理性能
PHYSICAL KPOL-HDPE HD K-10.0/948 Marlex® HXM 50100 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

抗环境应力开裂(100%非离子洗涤剂，模压成型，F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693B

抗环境应力开裂(50 ℃，1.91 mm，10%润湿剂)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693B

抗环境应力开裂(50 ℃，3.18 mm，100%润湿剂)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693A

熔体质量流动速率(190℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT KPOL-HDPE HD K-10.0/948 Marlex® HXM 50100 单位
UNIT 测试方法
TEST METHOD

拉伸冲击强度
Tensile impact strength kJ/m² ASTM D1822

拉伸冲击强度(模压成型)
Tensile impact strength kJ/m² ASTM D1822

热性能
THERMAL KPOL-HDPE HD K-10.0/948 Marlex® HXM 50100 单位
UNIT 测试方法
TEST METHOD

热变形温度
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，模压成型)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃ DSC

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 5

脆化温度
Embrittlement temperature ℃ ASTM D746

脆化温度
Embrittlement temperature ℃ ASTM D746A

机械性能
MECHANICAL KPOL-HDPE HD K-10.0/948 Marlex® HXM 50100 单位
UNIT 测试方法
TEST METHOD

弯曲模量(正切)
Bending modulus MPa ASTM D790

弯曲模量(正切，模压成型)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，模压成型)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服，模压成型)
tensile strength MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D，模压成型)
Shore hardness ASTM D2240

阻燃性能
FLAMMABILITY KPOL-HDPE HD K-10.0/948 Marlex® HXM 50100 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

备注

1 一般属性：这些不能被视为规格。

2 类型 4, 2.0 in/min

3 0.50 in/min

4 Type S

5 速率 A (50°C/h), 压力1 (10N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
阻燃性能
加工方式
备注