公司信息及水印
牌号简介 About |
---|
UL312采用Unipol工艺技术制造。UL312具有良好的力学性能,无凝胶和良好的加工性能。 UL312 is manufactured by Unipol process technology. UL312 has good mechanical properties, gel free and good processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
41.2 | MPa | ASTM D882 |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
37.3 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength 2 |
ASTM D1922 | ||
MD,40 µm MD,40 µm |
kN/m | ASTM D1922 | |
TD,40 µm TD,40 µm |
kN/m | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
松下推出新型密封及粘合资料 用于车载开关及传感器
2016-02-17 松下汽车电子和机电系统公司(Panasonic Automotive & Industrial Systems Company)将从2016年3月开始量产用于密封及粘合加工用途的材料“激光熔敷用聚对苯二甲酸丁二醇酯(PBT)树脂成型材料”。据介绍,使用该材料可减少车载设备用开关及传感器等的生产工序、提高长期可靠性及设计自由度。 为了使该材料产品化,该公司开发出了“合金化技术”,利用该技术可高效率透过、吸收激光,瞬间熔融,使海岛构造(含有多种成分的高分子相态的一种)均 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |