mLLDPE，Alkamax® ML1710SC对比mLLDPE，Alkamax® ML 1810PN物性表,价格行情_搜料

牌号信息	Alkamax® ML1710SC 物性表 mLLDPE & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货	Alkamax® ML 1810PN 物性表 mLLDPE & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货
牌号简介	ML1710SC是一种茂金属线性低密度聚乙烯共聚物。这种茂金属级是为高性能薄膜应用而设计的，要求具有优异的光学性能和韧性。ML1710SC采用工艺助剂和工艺稳定包配制。不含防滑或防堵塞添加剂。薄膜挤出：ML1710SC适用于需要高性能聚乙烯树脂的薄膜应用。用ML1710SC制备的薄膜，透明度高，光泽度高，韧性和密封性好。ML1710SC特别适用于含粘胶添加剂的吹塑拉伸薄膜。这一等级允许快速的黏附发展和更高的最终黏附水平，具有优异的抗穿刺性和韧性。如果预期的应用涉及间歇性到长时间暴露在阳光下，则应考虑添加紫外线稳定剂。 ML1710SC is a metallocene linear low density polyethylene copolymer. This metallocene grade is designed for high performance film applications requiring superior optical properties and toughness. ML1710SC is formulated with a process aid and a process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: ML1710SC is intended for film applications requiring high performance polyethylene resins. Films produced with ML1710SC have superior clarity and higher gloss, combined with excellent toughness and sealability. ML1710SC is particularly suitable for blown stretch films containing cling additives. This grade allows rapid cling development and a higher ultimate cling level, with excellent puncture resistance and toughness. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight.	Alkamax ML1810PN是一种茂金属线性低密度聚乙烯共聚物。这种茂金属品位具有良好的加工性能，可提高生产率。它是为高性能薄膜应用而设计的，要求最大的韧性和良好的密封性能。Alkamax ML1810PN采用工艺助剂和工艺稳定包配制而成。不含防滑或防堵塞添加剂。Alkamax ML1810PN适用于需要高性能聚乙烯树脂的应用。用Alkamax ML1810PN生产的薄膜具有优异的韧性，使其非常适合用于重型应用或对现有薄膜结构进行下测。此外，该等级的高性能密封和热粘性能结合其优良的光学性能，使其成为层压和成型、填充和密封薄膜的理想选择。它被设计用于各种吹塑薄膜挤出设备的加工。如果预期的应用涉及间歇性到长时间暴露在阳光下，则应考虑添加紫外线稳定剂。 Alkamax ML1810PN is a metallocene linear low density polyethylene copolymer. This metallocene grade has excellent processability permitting higher production rates. It is designed for high performance film applications requiring maximum toughness and excellent sealing performance. Alkamax ML1810PN is formulated with a process aid and process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: Alkamax ML1810PN is intended for applications requiring high performance polyethylene resins. Films produced with Alkamax ML1810PN have outstanding toughness, making this grade ideal for use in heavy duty applications or for downgauging existing film structures. In addition, the high performance sealing and hot tack properties of this grade combined with its excellent optical properties make it ideal for lamination and form, fill and seal films. It has been designed for processing on a wide range of blown film extrusion equipment. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight.

产品描述
厂家：	澳大利亚凯诺斯 Qenos	澳大利亚凯诺斯 Qenos
类别：	mLLDPE mLLDPE	mLLDPE mLLDPE
填料：
用途：	吹膜,薄膜	薄膜,层压板
性能特点：	耐候抗UV,易加工,透光性好,韧性好,表面光泽度好,低密度,共聚物,抗穿孔性,光学性能 Weather resistance is good,Excellent Processability,Good Clarity,Good flexibility,Good surface appearance,Low density,Copolymer,Puncture Resistant	耐候抗UV,易加工,韧性好,食品接触,密封范围宽,低密度,共聚物 Weather resistance is good,Excellent Processability,Good flexibility,Food contact compliance,Broad Seal Range,Low density,Copolymer
加工条件：	薄膜挤出 Film extrusion	薄膜挤出 Film extrusion

技术参数

物理性能
PHYSICAL Alkamax® ML1710SC Alkamax® ML 1810PN 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

薄膜
Alkamax® ML1710SC Alkamax® ML 1810PN 单位
UNIT 测试方法
TEST METHOD

割线模量(2% 正割，MD：50 µm)
Secant modulus MPa

割线模量(2% 正割，MD：50 µm)
Secant modulus MPa ASTM D882

割线模量(2% 正割，TD：50 µm)
Secant modulus MPa

割线模量(2% 正割，TD：50 µm)
Secant modulus MPa ASTM D882

埃尔曼多夫抗撕强度(MD：50 µm)
Elmandorf tear strength g

埃尔曼多夫抗撕强度(MD：50 µm)
Elmandorf tear strength g ASTM D1922

埃尔曼多夫抗撕强度(TD：50 µm)
Elmandorf tear strength g

埃尔曼多夫抗撕强度(TD：50 µm)
Elmandorf tear strength g ASTM D1922

拉伸应变(MD，断裂，50 µm)
Tensile strain %

拉伸应变(MD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，50 µm)
Tensile strain %

拉伸应变(TD，断裂，50 µm)
Tensile strain % ASTM D882

拉伸强度(MD，屈服，50 µm)
tensile strength MPa

拉伸强度(MD，屈服，50 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，50 µm)
tensile strength MPa

拉伸强度(MD，断裂，50 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，50 µm)
tensile strength MPa

拉伸强度(TD，屈服，50 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，50 µm)
tensile strength MPa

拉伸强度(TD，断裂，50 µm)
tensile strength MPa ASTM D882

落锤冲击
Drop hammer impact g ASTM D1709

落锤冲击(50 µm)
Drop hammer impact g ASTM D1709

薄膜厚度(测试)
film thickness µm

光学性能
OPTICAL Alkamax® ML1710SC Alkamax® ML 1810PN 单位
UNIT 测试方法
TEST METHOD

光泽度(45°)
gloss ASTM D2457

光泽度(45°，50 µm)
gloss ASTM D2457

雾度(50 µm)
Haze % ASTM D1003

备注

2、20 mm/min

3、500 mm/min

4、F50

1 一般属性：这些不能被视为规格。

2 0.79 in/min

3 20 in/min

4 F50

5 (10% LDPE blended)


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
光学性能
加工方式
备注
返回顶部

mLLDPE，Alkamax® ML1710SC对比mLLDPE，Alkamax® ML 1810PN对比物性表,价格行情_搜料_soliao