| 牌号简介 About |
|---|
| Alkamax ML1810PN是一种茂金属线性低密度聚乙烯共聚物。这种茂金属品位具有良好的加工性能，可提高生产率。它是为高性能薄膜应用而设计的，要求最大的韧性和良好的密封性能。Alkamax ML1810PN采用工艺助剂和工艺稳定包配制而成。不含防滑或防堵塞添加剂。Alkamax ML1810PN适用于需要高性能聚乙烯树脂的应用。用Alkamax ML1810PN生产的薄膜具有优异的韧性，使其非常适合用于重型应用或对现有薄膜结构进行下测。此外，该等级的高性能密封和热粘性能结合其优良的光学性能，使其成为层压和成型、填充和密封薄膜的理想选择。它被设计用于各种吹塑薄膜挤出设备的加工。如果预期的应用涉及间歇性到长时间暴露在阳光下，则应考虑添加紫外线稳定剂。 Alkamax ML1810PN is a metallocene linear low density polyethylene copolymer. This metallocene grade has excellent processability permitting higher production rates. It is designed for high performance film applications requiring maximum toughness and excellent sealing performance. Alkamax ML1810PN is formulated with a process aid and process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: Alkamax ML1810PN is intended for applications requiring high performance polyethylene resins. Films produced with Alkamax ML1810PN have outstanding toughness, making this grade ideal for use in heavy duty applications or for downgauging existing film structures. In addition, the high performance sealing and hot tack properties of this grade combined with its excellent optical properties make it ideal for lamination and form, fill and seal films. It has been designed for processing on a wide range of blown film extrusion equipment. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight. |
产品描述 Product Description
用途：薄膜;层压板;
加工条件：薄膜挤出 Film extrusion
性能特点： 共聚物; 食品接触; 耐候抗UV; 韧性好; 低密度; 密封范围宽; 易加工; Weather resistance is good,Excellent Processability,Good flexibility,Food contact compliance,Broad Seal Range,Low density,Copolymer
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
割线模量 Secant modulus 2 |
ASTM D882 | ||
|
2% 正割，MD：50 µm 2% secant, MD: 50 µ m |
183 | MPa | ASTM D882 |
|
2% 正割，TD：50 µm 2% secant, TD: 50 µ m |
190 | MPa | ASTM D882 |
|
拉伸强度 tensile strength 3 |
ASTM D882 | ||
|
MD，屈服，50 µm MD, yield, 50 µ m |
MPa | ASTM D882 | |
|
TD，屈服，50 µm TD, yield, 50 µ m |
MPa | ASTM D882 | |
|
MD，断裂，50 µm MD, fracture, 50 µ m |
MPa | ASTM D882 | |
|
TD，断裂，50 µm TD, fracture, 50 µ m |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
|
MD，断裂，50 µm MD, fracture, 50 µ m |
% | ASTM D882 | |
|
TD，断裂，50 µm TD, fracture, 50 µ m |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 4 |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：50 µm MD：50 µm |
g | ASTM D1922 | |
|
TD：50 µm TD：50 µm |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss 5 |
|||
|
45° 45° 5 |
ASTM D2457 | ||
|
雾度 Haze 5 |
|||
|
50 µm 50 µm 5 |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.79 in/min |
| 3 20 in/min |
| 4 F50 |
| 5 (10% LDPE blended) |
|
【新闻资讯】查看全部
淄博年消费40万吨叔丁醇
2018-11-02 10月26日，国内碳四深加工产业龙头，淄博齐翔腾达化工股份有限公司年生产40万吨叔丁醇及配套20万吨MMA、年生产10万吨PMMA项目暨年生产45万吨丙烷脱氢项目奠基仪式在淄博市齐鲁化工园区金山片区举行。这也是首届儒商大会签约项目中，淄博首个开工建设的项目。 此次奠基的两个项目均在2018年9月29日山东省首届儒商大会高端化工产业论坛上签约。其中，环保类高端化工项目40万吨/年叔丁醇及20万吨/年MMA、10万吨/年PMMA项目预计投资38亿元，建成投产后预计新增销售收入4 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付