Viton® A-331C
氟橡胶 & 美国科慕
Viton® GBL-600S
氟橡胶 & 美国科慕
高亮区别
隐藏相同
| 牌号信息 |
氟橡胶 & 美国科慕 指导价格：388500.0元/吨 塑料库存： 100kg 
|
氟橡胶 & 美国科慕 指导价格：暂无 塑料库存： 缺货
|
|
| 牌号简介 |
Viton® A-331C是一种“A系列”固化二聚物，设计用于注塑和转移需要改进的脱模“热撕裂”阻力的成型零件。中等粘度水平Viton® A-331C还允许零件满意的压缩成型。特点中等粘度水平（与相关的“O形环”聚合物氟橡胶A-202C和氟橡胶A-402C相比）完全预复合降低固化水平，加入工艺助剂，改进加工，提高模具流动性，减少模具污染，更好地释放模具，改进脱模，“热撕裂”良好的压缩永久性应用注射N、O型圈、密封件和垫圈的转移和压缩成型其他需要改进脱模的型材“热撕裂”挤压O型圈软线、软管和其他型材 Viton® A-331C is an incorporated cure "A-family" dipolymer designed for the injection and transfer of molding parts requiring improved demolding "hot tear" resistance. The moderate viscosity level of Viton® A-331C also allows for satisfactory compression molding of parts. Features Intermediate viscosity level (when compared with related "O-Ring" polymers Viton® A-202C and Viton® A-402C) Fully precompounded reduced curative level incorporated process aid Improved processing increased mold flow better mold release with less mold fouling improved demolding "hot tear" Good compression set resistance Applications Injection, transfer and compression molding of: O-rings, seals, and gaskets Other profiles requiring improved demolding "hot tear" Extruded O-ring cord, hose, and other profiles |
Viton® GBL-600S是一种新一代、易加工、过氧化固化的68%氟橡胶，基于新的先进聚合物结构技术。与原Viton GBL-900相比，Viton® GBL-600S具有可加工性，在芳烃、醇类、水、蒸汽和酸中具有类似或改进的流体阻力。与Viton GBL-900和Viton GBL-200相比，特性能快速固化到较高的固化状态，从而改善了模具的释放/污染性能，改善了模具流动性，降低了剪切敏感性，降低了65 Mooney FKM的挤出机模具膨胀，具有良好的物理性能和较高的延伸率，既有原始的，也有老化的。与Viton GBL-900和Viton GBL-200相比，TS具有相似的耐热性、耐流体性和耐低温性，在短时间（2小时）或无后固化的情况下具有优异的压缩永久变形性能。 Viton® GBL-600S is a next generation, easy processing, peroxide cured 68% fluorine fluoroelastomer based on new Advanced Polymer Architecture technology. Compared to the original Viton® GBL-900, Viton® GBL-600S exhibits processability coupled with similar or improved fluids resistance in aromatic hydrocarbons, alcohols, water, steam, and acids. Features Cures exceptionally fast to a high state of cure Exhibits improved mold release/mold fouling properties compared to Viton® GBL-900 and Viton® GBL-200 Exhibits improved mold flow, less shear sensitivity, and lower extruder die swell for a 65 Mooney FKM Exhibits excellent physical properties with high elongation, both original and aged Exhibits similar heat, fluids, and low temperature resistance compared to Viton® GBL-900 and Viton® GBL-200 Exhibits excellent compression set resistance with short (2 hr) or no postcure |
|
| 产品描述 | |||
| 厂家： | 美国科慕 Chemours | 美国科慕 Chemours | |
| 类别： | 氟橡胶 氟橡胶 | 氟橡胶 氟橡胶 | |
| 填料： | |||
| 用途： | 垫圈,O型圈,管道,管件,密封件,型材 | ||
| 性能特点： | 尺寸稳定性好,易流动,含脱模剂 Good Dimensional Stability,Good liquidity,Good stripping performance | 易加工,尺寸稳定性好,耐酒精,易流动,耐低温,含脱模剂,耐酸,拉伸性能好,耐蒸汽,耐碳氢化合物 Excellent Processability,Good Dimensional Stability,Ethanol tolerance,Good liquidity,Antifreeze,Good stripping performance,Acidproof,Good Tensile Strength,Resistance to the steam,Hydrocarbons | |
| 加工条件： | 挤出 Extrusion | ||
| 备注 |
1 一般属性：这些不能被视为规格。
2 20 in/min
3 20 in/min, 老化 70 hr 在 392°F
4 20 in/min, 老化 168 hr 在 392°F
5 20 in/min, 老化 24 hr 在 450°F
6 20 in/min, 老化 70 hr 在 450°F
7 老化 70 hr 在 392°F
8 老化 168 hr 在 392°F
9 老化 24 hr 在 450°F
10 老化 70 hr 在 450°F
|
1 一般属性：这些不能被视为规格。
2 508 mm/min, Aged 70 hr at 275°C
3 508 mm/min, Aged 168 hr at 150°C
4 508 mm/min, Aged 70 hr at 250°C
5 508 mm/min
6 508 mm/min, Aged 2 hr at 232°C
7 20 in/min
8 20 in/min, 老化 168 hr 在 302°F
9 20 in/min, 老化 2 hr 在 450°F
10 20 in/min, 老化 70 hr 在 482°F
11 20 in/min, 老化 70 hr 在 527°F
12 B 模具
13 Nicked
14 Postcured at 232°C
15 老化 168 hr 在 302°F
16 老化 2 hr 在 450°F
17 老化 70 hr 在 482°F
18 老化 70 hr 在 527°F
|
价格走势对比图
氟橡胶 Viton® A-331C
氟橡胶 Viton® GBL-600S
| 型号 | 类别 | 厂家 | 产地 | 颜色 | 首期使用量 | 后期使用量 | 包装 | 交期 | 成型产品 | 操作 |
|---|---|---|---|---|---|---|---|---|---|---|
| GP-525N | GPPS | VATAA土耳其地区 | 亚太地区 | 天 |
单据状态：未提交
| 牌号 | 类别 | 厂家 |
|---|
| 暂无数据 |
Copyright@ 2015- soliao.com All Right Reserved
增值电信业务经营许可证： 粤B2-20220577号 |
备案号： 粤ICP备16019933号 | 广州搜料信息技术有限公司@版权所有