| 牌号简介 About |
|---|
| Viton® A-331C是一种“A系列”固化二聚物，设计用于注塑和转移需要改进的脱模“热撕裂”阻力的成型零件。中等粘度水平Viton® A-331C还允许零件满意的压缩成型。特点中等粘度水平（与相关的“O形环”聚合物氟橡胶A-202C和氟橡胶A-402C相比）完全预复合降低固化水平，加入工艺助剂，改进加工，提高模具流动性，减少模具污染，更好地释放模具，改进脱模，“热撕裂”良好的压缩永久性应用注射N、O型圈、密封件和垫圈的转移和压缩成型其他需要改进脱模的型材“热撕裂”挤压O型圈软线、软管和其他型材 Viton® A-331C is an incorporated cure "A-family" dipolymer designed for the injection and transfer of molding parts requiring improved demolding "hot tear" resistance. The moderate viscosity level of Viton® A-331C also allows for satisfactory compression molding of parts. Features Intermediate viscosity level (when compared with related "O-Ring" polymers Viton® A-202C and Viton® A-402C) Fully precompounded reduced curative level incorporated process aid Improved processing increased mold flow better mold release with less mold fouling improved demolding "hot tear" Good compression set resistance Applications Injection, transfer and compression molding of: O-rings, seals, and gaskets Other profiles requiring improved demolding "hot tear" Extruded O-ring cord, hose, and other profiles |
产品描述 Product Description
用途：管道;密封件;型材;O型圈;垫圈;管件;
颜色：白色
加工条件：挤出 Extrusion
性能特点： 尺寸稳定性好; 含脱模剂; 易流动; Good Dimensional Stability,Good liquidity,Good stripping performance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.82 | g/cm³ | ASTM D792 |
|
表观密度 Apparent density |
1.82 | g/cm³ | ASTM D1895 |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+10，121℃ ML 1+10，121℃ |
65 | MU | ASTM D1646 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ |
71 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 2 |
75 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 3 |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ 4 |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ 5 |
ASTM D2240 | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
100% 应变，23℃ 100% strain, 23 ℃ 6 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 7 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 8 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 9 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 10 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
屈服，23℃ Yield, 23 ℃ 6 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 7 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 8 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 9 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 10 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂，23℃ Fracture, 23 ℃ 6 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 7 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 8 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 9 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 10 |
% | ASTM D412 | |
|
压缩形变 Compression deformation |
ASTM D395B | ||
|
23℃，70 hr 23℃，70 hr |
% | ASTM D395B | |
|
200℃，70 hr 200℃，70 hr |
% | ASTM D395B | |
|
200℃，168 hr 200℃，168 hr |
% | ASTM D395B | |
|
232℃，70 hr 232℃，70 hr |
% | ASTM D395B | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 20 in/min |
| 3 20 in/min, 老化 70 hr 在 392°F |
| 4 20 in/min, 老化 168 hr 在 392°F |
| 5 20 in/min, 老化 24 hr 在 450°F |
| 6 20 in/min, 老化 70 hr 在 450°F |
| 7 老化 70 hr 在 392°F |
| 8 老化 168 hr 在 392°F |
| 9 老化 24 hr 在 450°F |
| 10 老化 70 hr 在 450°F |
|
【新闻资讯】查看全部 
"Nordson将于 2020 年年底完成其挤出和流体涂布模头业务全球中心的树立"
2018-11-14 Nordson Corporation 近日举行仪式，庆祝了其 Extrusion Dies Industries挤出产品线和Premier流体涂布产品线的新全球总部的破土活动，这些产品线包括用于提高模头质量的先进设备和为客户提供服务的更加高效的系统。 这座占地面积达 145,000 平方英尺(13,500 平方米)的工厂将位于奇普瓦瀑布市工业园区中三个现有的 Nordson工厂附近，其中包括目前的 Extrusion Dies Industries 总部和挤出模头制造厂; |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付