技术参数
物理性能 PHYSICAL
LEXAN™ HP1R resin
LEXAN™ HP1 resin
单位 UNIT
测试方法 TEST METHOD
吸水率(24hr)
Water absorption rate
%
ASTM D570
吸水率(平衡,100℃)
Water absorption rate
%
ASTM D570
吸水率(平衡,23℃)
Water absorption rate
%
ASTM D570
密度
Density
g/cm³
ASTM D792
收缩率(MD:3.2 mm)
Shrinkage rate
%
内部方法
熔体体积流动速率(300℃,1.2 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体质量流动速率(300℃,1.20kg)
Melt Flow Rate
g/10min
ASTM D1238
特定体积
Specific volume
cm³/g
ASTM D792
冲击性能 IMPACT
LEXAN™ HP1R resin
LEXAN™ HP1 resin
单位 UNIT
测试方法 TEST METHOD
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D4812
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(Natural,Tints)
Impact strength of cantilever beam notch
J/m
ASTM D256
拉伸冲击强度
Tensile impact strength
kJ/m²
ASTM D1822
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
落锤冲击(23℃)
Drop hammer impact
J
ASTM D3029
装有测量仪表的落镖冲击(23℃,Energy at Peak Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能 THERMAL
LEXAN™ HP1R resin
LEXAN™ HP1 resin
单位 UNIT
测试方法 TEST METHOD
导热系数
Thermal conductivity coefficient
W/m/K
ASTM C177
导热系数
Thermal conductivity coefficient
W/m/K
ISO 8302
比热
specific heat
J/kg/℃
ASTM C351
热变形温度(0.45 MPa,未退火,100 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Be
热变形温度(0.45 MPa,未退火,6.4 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,100 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Ae
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,6.4 mm)
Hot deformation temperature
℃
ASTM D648
球压测试(125℃)
Ball pressure test
IEC 60695-10-2
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746
相对温度指数(强度机械性能)
Relative temperature index
℃
UL 746
相对温度指数(电气性能)
Relative temperature index
℃
UL 746
线性热膨胀系数(MD:-40~95℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(MD:23~80℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
维卡软化温度(A50)
Vicat Softening Temp
℃
ISO 306/A50
维卡软化温度(B120)
Vicat Softening Temp
℃
ISO 306/B120
维卡软化温度(B50)
Vicat Softening Temp
℃
ISO 306
电气性能 ELECTRICAL
LEXAN™ HP1R resin
LEXAN™ HP1 resin
单位 UNIT
测试方法 TEST METHOD
介电常数(1 MHz)
Dielectric constant
ASTM D150
介电常数(50 Hz)
Dielectric constant
ASTM D150
介电常数(60 Hz)
Dielectric constant
ASTM D150
介电强度(0.8 mm,在油中)
Dielectric strength
kV/mm
IEC 60243-1
介电强度(1.6 mm,在油中)
Dielectric strength
kV/mm
IEC 60243-1
介电强度(3.2 mm,在油中)
Dielectric strength
kV/mm
IEC 60243-1
介电强度(3.2 mm,在空气中)
Dielectric strength
kV/mm
ASTM D149
体积电阻率
Volume resistivity
ohms·cm
ASTM D257
体积电阻率
Volume resistivity
ohms·cm
IEC 60093
热丝引燃(HWI)
Hot wire ignition
UL 746
相对电容率(1 MHz)
Relative permittivity
IEC 60250
相对电容率(50 Hz)
Relative permittivity
IEC 60250
相对电容率(60 Hz)
Relative permittivity
IEC 60250
相比漏电起痕指数
Compared to the leakage tracing index
UL 746
耗散因数(1 MHz)
Dissipation factor
ASTM D150
耗散因数(1 MHz)
Dissipation factor
IEC 60250
耗散因数(50 Hz)
Dissipation factor
ASTM D150
耗散因数(50 Hz)
Dissipation factor
IEC 60250
耗散因数(60 Hz)
Dissipation factor
ASTM D150
耗散因数(60 Hz)
Dissipation factor
IEC 60250
表面电阻率
Surface resistivity
ohms
IEC 60093
高电压电弧起痕速率(HVTR)
High voltage arc marking rate
UL 746
高电弧燃烧指数(HAI)
High Arc Burning Index (HAI)
UL 746
阻燃性能 FLAMMABILITY
LEXAN™ HP1R resin
LEXAN™ HP1 resin
单位 UNIT
测试方法 TEST METHOD
1.10 mm
1.10 mm
UL 94
极限氧指数
Extreme oxygen index
%
ISO 4589-2
光学性能 OPTICAL
LEXAN™ HP1R resin
LEXAN™ HP1 resin
单位 UNIT
测试方法 TEST METHOD
折射率
Refractive index
ASTM D542
透光率(2540 µm)
Transmittance
%
ASTM D1003
雾度(2540 µm)
Haze
%
ASTM D1003
机械性能 MECHANICAL
LEXAN™ HP1R resin
LEXAN™ HP1 resin
单位 UNIT
测试方法 TEST METHOD
弯曲强度
bending strength
MPa
ISO 178
弯曲强度(屈服,50 mm跨度)
bending strength
MPa
ASTM D790
弯曲模量(50 mm跨距)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/50
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/50
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/50
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/50
拉伸模量
Tensile modulus
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ISO 527-1-2
泰伯耐磨性(1000 周期,1000 g,CS-17 转轮)
Taber abraser
mg
ASTM D1044
洛氏硬度(M 级)
Rockwell hardness
ASTM D785
洛氏硬度(R 级)
Rockwell hardness
ASTM D785