技术参数
物理性能 PHYSICAL
Solef® 11010
Solef® 6010
单位 UNIT
测试方法 TEST METHOD
吸水率 Water Absorption(23℃,24hr)
Water Absorption
%
ASTM D570
吸水率(23℃,24hr)
Water absorption rate
%
ASTM D570
密度
Density
g/cm³
ASTM D792
密度 Density
Density
g/cm³
ASTM D792
收缩率 Shrinkage(MD)
Shrinkage rate
%
收缩率(MD)
Shrinkage rate
%
熔体质量流动速率 Melt Flow Rate(230℃,5.0kg)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(230℃,5.0kg)
Melt Flow Rate
g/10min
ASTM D1238
机械性能 MECHANICAL
Solef® 11010
Solef® 6010
单位 UNIT
测试方法 TEST METHOD
拉伸应变 Tensile Strain(屈服 yld,23℃,2 mm)
Tensile Strain
%
ASTM D638
拉伸应变 Tensile Strain(断裂 brk,23℃,2 mm)
Tensile Strain
%
ASTM D638
拉伸应变(屈服,23℃,2 mm)
Tensile strain
%
ASTM D638
拉伸应变(断裂,23℃,2 mm)
Tensile strain
%
ASTM D638
拉伸强度 Tensile Strength(屈服 yld,23℃,2 mm)
Tensile Strength
MPa
ASTM D638
拉伸强度 Tensile Strength(断裂 brk,23℃,2 mm)
Tensile Strength
MPa
ASTM D638
拉伸强度(屈服,23℃,2 mm)
tensile strength
MPa
ASTM D638
拉伸强度(断裂,23℃,2 mm)
tensile strength
MPa
ASTM D638
拉伸模量 Tensile Modulus(23℃,2 mm)
Tensile Modulus
MPa
ASTM D638
拉伸模量(23℃,2 mm)
Tensile modulus
MPa
ASTM D638
摩擦系数 Frictional coefficient(与自身 - 动态)
Frictional coefficient
ASTM D1894
摩擦系数 Frictional coefficient(与自身 - 静态)
Frictional coefficient
ASTM D1894
摩擦系数(与自身 - 动态)
friction coefficient
ASTM D1894
摩擦系数(与自身 - 静态)
friction coefficient
ASTM D1894
泰伯耐磨性 Taber Abrasion(1000 周期,1000 g,CS-10 转轮)
Taber Abrasion
mg
ASTM D4060
泰伯耐磨性(1000 周期,1000 g,CS-10 转轮)
Taber abraser
mg
ASTM D4060
邵氏硬度 Shore hardness(邵氏 D,1 秒,2.00 mm)
Shore hardness
ASTM D2240
邵氏硬度(邵氏 D,1 秒,2.00 mm)
Shore hardness
ASTM D2240
冲击性能 IMPACT
Solef® 11010
Solef® 6010
单位 UNIT
测试方法 TEST METHOD
简支梁缺口冲击强度 Charpy notched Impact strength(23℃,4mm)
Charpy Notched Impact Strength
J/m
ASTM D6110
简支梁缺口冲击强度(23℃,4mm)
Charpy Notched Impact Strength
J/m
ASTM D6110
热性能 THERMAL
Solef® 11010
Solef® 6010
单位 UNIT
测试方法 TEST METHOD
导热系数 Thermal Conductivity(23℃)
Thermal conductivity
W/m/K
ASTM C177
导热系数(23℃)
Thermal conductivity coefficient
W/m/K
ASTM C177
峰值结晶温度(DSC) Peak Crystallization Temperature (DSC)(DSC)
Peak Crystallization Temperature (DSC)
℃
ASTM D3418
比热 Specific Heat(100℃)
Specific Heat
J/kg/℃
ASTM E968
比热 Specific Heat(23℃)
Specific Heat
J/kg/℃
ASTM E968
比热(100℃)
specific heat
J/kg/℃
ASTM E968
比热(23℃)
specific heat
J/kg/℃
ASTM E968
熔化热 Heat of Fusion
Heat of Fusion
J/g
ASTM D3417
熔融温度
Melting temperature
℃
ASTM D3418
熔融温度 Melting temperature
Melting temperature
℃
ASTM D3418
玻璃化转变温度
Glass transition temperature
℃
ASTM D4065
玻璃化转变温度 Glass Transition Temperature
Glass Transition Temperature
℃
ASTM D4065
线性热膨胀系数 Coeff.of linear therm expansion(MD:0~40℃)
Coeff. of linear thermal expansion
1/℃
ASTM D696
线性热膨胀系数(MD:0~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM D696
结晶峰温度(DSC)
Crystallization peak temperature
℃
ASTM D3418
结晶热
Crystallization heat
J/g
ASTM D3417
结晶热 Crystallization Heat
Crystallization Heat
J/g
ASTM D3417
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525 5
维卡软化温度 Vicat Softening Temperature
Vicat Softening Temperature
℃
ASTM D1525 5
融合热量
Fusion heat
J/g
ASTM D3417
电气性能 ELECTRICAL
Solef® 11010
Solef® 6010
单位 UNIT
测试方法 TEST METHOD
介电常数 Dielectric Constant(23 ℃,1 MHz)
Dielectric Constant
ASTM D150
介电常数(23 ℃,1 kHz)
Dielectric constant
ASTM D150
介电强度 Dielectric Strength(23 ℃,1 mm)
Dielectric Strength
kV/mm
ASTM D149
介电强度(23 ℃,1 mm)
Dielectric strength
kV/mm
ASTM D149
体积电阻率
Volume resistivity
ohms·cm
ASTM D257
体积电阻率 Volume Resistivity
Volume Resistance
ohms·cm
ASTM D257
耗散因数 Dissipation Factor(23℃,1 MHz)
Dissipation Factor
ASTM D150
表面电阻率
Surface resistivity
ohms
ASTM D257
表面电阻率 Surface Resistivity
Surface Resistivity
ohms
ASTM D257
阻燃性能 FLAMMABILITY
Solef® 11010
Solef® 6010
单位 UNIT
测试方法 TEST METHOD
0.10 mm
0.10 mm
UL 94
极限氧指数(3.0 mm)
Extreme oxygen index
%
ASTM D2863
阻燃等级 Flame Class Rating(0.10 mm)
Flame Class Rating
UL 94