| 牌号简介 About |
|---|
| solef ® 11010 PVDF是一种中等粘度韧性PVDF共聚物树脂，通常采用挤塑加工。 Solef® 11010 PVDF is a medium-viscosity flexible PVDF copolymer resin and is typically processed by extrusion. |
产品描述 Product Description
加工条件：挤出 Extrusion
性能特点： 防火阻燃等级V-0; 共聚物; 韧性好; V-0,Good flexibility,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density Density |
1.75 to 1.80 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
|
230℃，5.0kg 230℃，5.0kg |
4.0 to 8.0 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage Shrinkage rate |
|||
|
MD MD |
2.0 to 3.0 | % | |
|
吸水率 Water Absorption Water Absorption |
|||
|
23℃，24hr 23℃，24hr |
< 0.040 | % | ASTM D570 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness Shore hardness |
|||
|
邵氏 D，1 秒，2.00 mm Shore D, 1 second, 2.00 mm |
70 to 75 | ASTM D2240 | |
|
拉伸模量 Tensile Modulus Tensile Modulus |
|||
|
23℃，2 mm 23℃，2 mm |
MPa | ASTM D638 | |
|
拉伸强度 Tensile Strength Tensile Strength |
|||
|
断裂 brk，23℃，2 mm Broken BRK, 23 ℃, 2 mm |
MPa | ASTM D638 | |
|
屈服 yld，23℃，2 mm Yield yld, 23 ℃, 2 mm |
MPa | ASTM D638 | |
|
拉伸应变 Tensile Strain Tensile Strain |
|||
|
断裂 brk，23℃，2 mm Broken BRK, 23 ℃, 2 mm |
% | ASTM D638 | |
|
屈服 yld，23℃，2 mm Yield yld, 23 ℃, 2 mm |
% | ASTM D638 | |
|
摩擦系数 Frictional coefficient Frictional coefficient |
ASTM D1894 | ||
|
与自身 - 动态 With oneself - dynamic |
ASTM D1894 | ||
|
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
|
泰伯耐磨性 Taber Abrasion Taber Abrasion |
|||
|
1000 周期，1000 g，CS-10 转轮 1000 cycles, 1000 g, CS-10 wheels |
mg | ASTM D4060 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
|
23℃，4mm 23℃，4mm |
J/m | ASTM D6110 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ASTM D4065 | |
|
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 5 | |
|
熔融温度 Melting temperature Melting temperature |
℃ | ASTM D3418 | |
|
峰值结晶温度（DSC） Peak Crystallization Temperature (DSC) Peak Crystallization Temperature (DSC) |
|||
|
DSC DSC |
℃ | ASTM D3418 | |
|
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
|
MD：0~40℃ MD：0~40℃ |
1/℃ | ASTM D696 | |
|
比热 Specific Heat Specific Heat |
ASTM E968 | ||
|
23℃ 23℃ |
J/kg/℃ | ASTM E968 | |
|
100℃ 100℃ |
J/kg/℃ | ASTM E968 | |
|
导热系数 Thermal Conductivity Thermal conductivity |
|||
|
23℃ 23℃ |
W/m/K | ASTM C177 | |
|
结晶热 Crystallization Heat Crystallization Heat |
J/g | ASTM D3417 | |
|
熔化热 Heat of Fusion Heat of Fusion |
J/g | ASTM D3417 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface Resistivity Surface Resistivity |
ohms | ASTM D257 | |
|
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric Strength Dielectric Strength |
|||
|
23 ℃，1 mm 23 ℃，1 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric Constant Dielectric Constant |
|||
|
23 ℃，1 MHz 23 ℃，1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation Factor Dissipation Factor |
|||
|
23℃，1 MHz 23℃，1 MHz |
ASTM D150 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating Flame Class Rating |
|||
|
0.10 mm 0.10 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
|||
|
3.0 mm 3.0 mm |
% | ASTM D2863 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 类型 4, 0.039 in/min |
| 3 类型 4, 2.0 in/min |
| 4 2 m/s |
| 5 速率 A (50°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
从航天飞机到手机外壳：碳纤维的最新运用
2016-12-01 碳纤维已经在人们的生活之中发挥出巨大作用。其用途之广，达到高精尖的的长征五号、高铁、汽车、自行车等产品，小到羽毛球拍、钱包、手机外壳。下面我们就来看看离我们最近的几款最新应用吧。 碳纤维躺椅，瞄准男性富裕阶层 近日，日本开发出一种使用碳纤维材料的躺椅，预计将于今年12月中旬在日本上市。据报道，使用碳纤维材料的家具在欧洲已经开始成为潮流，这款碳纤维躺椅瞄准了男性富裕阶层。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付