PP均聚，EVALENE® PP PHT0171对比PP均聚，TOTAL Polypropylene PPH 3060物性表,价格行情_搜料

牌号信息	EVALENE® PP PHT0171 物性表 PP均聚 & 菲律宾JG Summit 指导价格：暂无塑料库存：缺货	TOTAL Polypropylene PPH 3060 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	evalene pht0171是专门为热成型而开发的，适用于需要高冲击强度和良好刚度的广泛挤压应用。该树脂完全采用成核剂配制而成，可缩短循环时间，并有机会改善最终产品的外观。evalene pht0171是需要热过滤和微波兼容性的容器的理想选择。特点：高冲击强度，良好的硬度，良好的循环时间，良好的透明度，满足菲律宾FDA食品接触要求，清真认证，典型应用，食品包装托盘和容器，饮料杯，衬垫托盘，刚性板。 EVALENE® PHT0171 is specifi cally developed for thermoforming and is intended for use in a broad range of extrusion applications requiring high impact strength and good stiffness. This resin is fully formulated with a nucleating agent resulting in improved cycle times as well as opportunities for enhanced end-product appearance. EVALENE® PHT0171 is ideal for containers requiring hot-fi ll and microwave compatibility. FEATURES High Izod Impact strength Good stiffness Good cycle times Good transparency Meets Philippine FDA food contact requirements Halal-certified TYPICAL APPLICATIONS Food Packaging Trays and Containers Drinking Cups Dunnage Trays Rigid Sheets	聚丙烯PPH 3060是均聚物，熔融流动指数为1.8 g/10 min。聚丙烯PPH 3060具有低流动性，用于连续挤压捆扎带、绳索纤维和高强度袋装胶带的特点。它也很好地设计用于吹塑或挤压热成型。 Polypropylene PPH 3060 is homopolymer with a Melt Flow Index of 1.8 g/10 min. Polypropylene PPH 3060 is characterized by a low fluidity for continuous extrusion of strapping, rope fibers and high tenacity tapes for bags. It is also well designed for blow molding or extrusion-thermoforming.

产品描述
厂家：	菲律宾JG Summit	法国道达尔 TOTAL
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	片材,容器,食品包装,杯子	绳索,皮带材料,纤维,带子
性能特点：	机械强度好,透光性好,韧性好,冲击性能好,成核的,食品接触,均聚物 Good Rigidity,Good Clarity,Good flexibility,High impact resistance,Nucleation,Food contact compliance,Homopolymer	流动性低,均聚物 Low liquidity,Homopolymer
加工条件：	挤出 Extrusion	挤出 Extrusion

技术参数

物理性能
PHYSICAL EVALENE® PP PHT0171 TOTAL Polypropylene PPH 3060 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 1183

冲击性能
IMPACT EVALENE® PP PHT0171 TOTAL Polypropylene PPH 3060 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL EVALENE® PP PHT0171 TOTAL Polypropylene PPH 3060 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL EVALENE® PP PHT0171 TOTAL Polypropylene PPH 3060 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(1% 正割)
Bending modulus MPa ASTM D790-A

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(1% 正割)
Tensile modulus MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

加工方式

挤出 EVALENE® PP PHT0171 TOTAL Polypropylene PPH 3060 单位测试方法

熔体温度 °C

备注

2 5.0 mm/min

3 50 mm/min

4 1.3 mm/min

5 Partial Break

6 DSC, 10°C/min, 2nd heating

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
加工方式
挤出
备注