| 牌号简介 About |
|---|
| evalene pht0171是专门为热成型而开发的，适用于需要高冲击强度和良好刚度的广泛挤压应用。该树脂完全采用成核剂配制而成，可缩短循环时间，并有机会改善最终产品的外观。evalene pht0171是需要热过滤和微波兼容性的容器的理想选择。特点：高冲击强度，良好的硬度，良好的循环时间，良好的透明度，满足菲律宾FDA食品接触要求，清真认证，典型应用，食品包装托盘和容器，饮料杯，衬垫托盘，刚性板。 EVALENE® PHT0171 is specifi cally developed for thermoforming and is intended for use in a broad range of extrusion applications requiring high impact strength and good stiffness. This resin is fully formulated with a nucleating agent resulting in improved cycle times as well as opportunities for enhanced end-product appearance. EVALENE® PHT0171 is ideal for containers requiring hot-fi ll and microwave compatibility. FEATURES High Izod Impact strength Good stiffness Good cycle times Good transparency Meets Philippine FDA food contact requirements Halal-certified TYPICAL APPLICATIONS Food Packaging Trays and Containers Drinking Cups Dunnage Trays Rigid Sheets |
产品描述 Product Description
用途：杯子;片材;容器;食品包装;
加工条件：挤出 Extrusion
性能特点： 成核的; 机械强度好; 均聚物; 透光性好; 食品接触; 冲击性能好; 韧性好; Good Rigidity,Good Clarity,Good flexibility,High impact resistance,Nucleation,Food contact compliance,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
1.7 | g/10min | ASTM D1238 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 5 |
|||
|
23℃ 23℃ 5 |
18 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
120 | ℃ | ASTM D648 |
|
熔融温度 Melting temperature 6 |
162 | ℃ | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
103 | ASTM D785 | |
|
拉伸模量 Tensile modulus 2 |
|||
|
1% 正割 1% secant 2 |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength 3 |
ASTM D638 | ||
|
屈服 yield |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 3 |
ASTM D638 | ||
|
屈服 yield |
% | ASTM D638 | |
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 4 |
|||
|
1% 正割 1% secant 4 |
MPa | ASTM D790-A | |
| 备注 |
|---|
| 2 5.0 mm/min |
| 3 50 mm/min |
| 4 1.3 mm/min |
| 5 Partial Break |
| 6 DSC, 10°C/min, 2nd heating |
|
【新闻资讯】查看全部 
【全球首款】ALPLA碳中和rPET树脂亮相
2020-10-24 搜料网资讯： ALPLA集团将其位于奥地利W?llersdorf和波兰Radomsko的PET回收团队工厂改为使用可再生能源的混合电力，以生产碳中和的回收聚对苯二甲酸乙二醇酯（rPET）。 这一步已经对我们 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付