牌号简介 About |
---|
Noryl FP3060是一种未填充、可注射成型的改性聚苯醚树脂。该树脂设计具有良好的尺寸稳定性和高流动性,还使用无氯化、无溴FR添加剂,以达到1.5 mm时的v1 ul94额定值和2.5 mm时的v0,比密度为1.1 g/cm^3。Noryl FP3060可能是平板电视外壳应用的优秀候选材料,要求具有良好的流变性能、耐热性、抗水解性、低密度和薄壁阻燃性。 NORYL FP3060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm and V0@ 2.5mm with a specific density of 1.1 g/cm^3. NORYL FP3060 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,3.80kg 200℃,3.80kg |
42 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
300℃,1.2 kg 300℃,1.2 kg |
20.0 | cm³/10min | |
280℃,2.16 kg 280℃,2.16 kg |
41.0 | cm³/10min | |
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
0.13 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 9 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 10 |
|||
23℃ 23℃ 10 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 11 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 12 |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 13 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 14 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831, ISO 11359-2 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
|||
2.50 mm 2.50 mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
标准注塑模具开发流程是什么样子的?
2018-04-08 一、绘制模具图 在画模具总装图之前,应绘制工序图,并要符合制件图和工艺资料的要求。由下道工序保证的尺寸,应在图上标写注明"工艺尺寸"字样。如果成型后除了修理毛刺之外,再不进行其他机械加工,那么工序图就与制件图完全相同。 在工序图下面最好标出制件编号、名称、材料、材料收缩率、绘图比例等。通常就把工序图画在模具总装图上。 绘制总装图尽量采用1:1的比例,先由型腔开 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |