牌号简介 About |
---|
Sarlink® TPV 3450N是一种高性能NSF 61认证的热塑性硫化胶,用于各种汽车、消费品和工业饮用水应用。Sarlink® TPV 3450N是一种中等硬度,低密度等级,具有优异的流体阻力和高温性能。它可以通过注射成型,吹塑或挤压加工与饮用水接触的应用,如管道,配件和附件。 Sarlink TPV 3450N is a general purpose thermoplastic vulcanizate used in consumer and industrial applications. Sarlink TPV 3450N is a low hardness, low density, RoHS compliant grade suitable for injection molding, blow molding, extrusion, and pipe extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
0.938 | g/cm³ | ASTM D792 |
-- -- |
0.940 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 , ISO 868 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
54 | ASTM D2240 , ISO 868 | |
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
57 | ASTM D2240 , ISO 868 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 , ISO 37 | ||
TD,100% 应变 TD, 100% strain |
1.80 | MPa | ASTM D412 , ISO 37 |
MD,100% 应变 MD, 100% strain |
MPa | ASTM D412 , ISO 37 | |
拉伸强度 tensile strength |
|||
TD,屈服 TD, yield |
MPa | ASTM D412 | |
MD,屈服 MD, yield |
MPa | ASTM D412 | |
TD,断裂 TD, fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
ASTM D412 , ISO 37 | ||
TD,断裂 TD, fracture |
% | ASTM D412,ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ASTM D412,ISO 37 | |
撕裂强度 tear strength |
|||
TD TD 2 |
kN/m | ASTM D624 | |
TD TD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
|||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B,ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B,ISO 815 | |
100℃,22 hr 100℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
|||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 , ISO 188 | |
100% 应变,135℃,1000 hr 100% strain, 135 ℃, 1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 , ISO 188 | |
100% 应变,150℃,168 hr 100% strain, 150 ℃, 168 hr |
% | ASTM D573 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ISO 188 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
TD:135℃,1000 hr TD:135℃,1000 hr |
% | ASTM D573 | |
TD:150℃,168 hr TD:150℃,168 hr |
% | ASTM D573 | |
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 , ISO 188 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ASTM D573 , ISO 188 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ASTM D573 , ISO 188 | ||
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 , ISO 1817 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体表观粘度 - Capillary,@ 206/s Apparent viscosity of melt - Capillary, @ 206/s |
|||
200℃ 200℃ |
Pa·s | ASTM D3835 | |
200℃ 200℃ |
Pa·s | ISO 11443 |
备注 |
---|
2 C 模具 |
【新闻资讯】查看全部
汉高增长议程战略获进展
2021-08-28 搜料网资讯: 近日,汉高首席执行官卡斯滕诺贝尔表示,除积极的产品组合管理,汉高今年上半年一直在实施其增长议程战略,即通过进一步加强创新、可持续发展和数字化领域的实力 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |