| 牌号简介 About |
|---|
| Queo™ 1001是一种乙烯基辛烯塑料，在溶液聚合过程中使用茂金属催化剂生产。Queo™ 1001是其他聚烯烃在薄膜、挤压和成型应用中的多功能混合伙伴，提供：无与伦比的密封性能、优异的韧性、耐刺穿性和低温冲击强度、优异的聚烯烃兼容性、柔韧性、优异的耐环境应力开裂性、低提取量高清晰度应用：示范应用包括：层压密封层和柔性阻挡膜高强度柔性膜柔性低压绝缘吹塑制品柔性汽车靴和波纹管软泡沫添加剂：Queo™ 1001含有加工稳定剂。 Queo 1001 is an ethylene based octene-1 plastomer, produced in a solution polymerisation process using a metallocene catalyst. CAS-No.: 26221-73-8 Applications Queo 1001 Demonstrated applications include: Seal layers in lamination and flexible barrier films Blow moulding High strength flexible films Soft foams, e.g. artificial wine corks Flexible low voltage insulation Flexible automotive boots and bellows Additives Queo 1001 contains processing stabilizers Special Features Queo 1001 is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. Outstanding puncture resistance Low temperature impact strength Unrivalled sealing and hot tack properties at low temperature High flexibility and surface softness High clarity Outstanding toughness Excellent environmental stress cracking resistance (ESCR) |
产品描述 Product Description
用途：汽车领域的应用;密封件;泡沫;
加工条件：挤出 Extrusion
性能特点： 机械强度好; 耐低温冲击; 透光性好; 抗应力开裂; 韧性好; 抗穿孔性; Good Rigidity,Good Clarity,Good flexibility,low-temperature impact resistance,Puncture Resistant,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.910 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.1 | g/10min | ISO 1133 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
> 1000 | hr | ASTM D1693B |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
49 | ISO 868 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
35.0 | MPa | ISO 527-2/5A |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/5A | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus |
|||
|
MD MD |
MPa | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
吹塑薄膜 Blown film |
g | ASTM D1709 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
ISO 180/1A | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 11357 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45° 45° |
ASTM D2457 | ||
|
雾度 Haze |
% | ASTM D1003A | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
抗穿刺性 Puncture resistance |
J/cm | Internal Method | |
|
Sealing Initial Temperature Sealing Initial Temperature |
℃ | ASTM F88 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
扬子石化长玻纤加强聚丙烯完成替代进口
2019-01-31 1月17日至19日，扬子石化塑料厂采纳了扬子研究院的改进质量建议，进行长玻纤增强 聚丙烯 专用料工业化生产，顺利解决了粒子外观问题，产品性能稳定，质量进一步提升，基本达到了 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付