Sarlink® TPE ME-1345N是一种热塑性弹性体(TPE)材料,。 该产品在亚太地区、北美洲、拉丁美洲、欧洲或非洲和中东有供货,加工方式为:挤出或注射成型。 Sarlink® TPE ME-1345N的主要特性为:通过 ROHS 认证。 Sarlink® TPE ME-1345N的典型应用领域为:汽车行业 Sarlink ME-1345N is a general purpose thermoplastic elastomer used in automotive applications, including exterior. Sarlink ME-1345N is a medium hardness, low density, lubricated grade that can be processed by injection molding and extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
断裂 fracture |
5.80 | MPa | ISO 37 |
MD,断裂 MD, fracture |
1.90 | MPa | ISO 37 |
TD,100% 应变 TD, 100% strain |
0.73 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
1.36 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
断裂 fracture |
820 | % | ISO 37 |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
kN/m | ISO 34-1 | |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 4 |
ISO 815 | ||
22℃,70 hr 22℃,70 hr |
% | ISO 815 | |
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
90℃,70 hr 90℃,70 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,1 秒,注塑成型 Shore A, 1 second, injection molding |
ISO 868 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ISO 868 | ||
邵氏 A,15 秒,注塑成型 Shore A, 15 seconds, injection molding |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ISO 188 | |
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
MD:125℃,168 hr MD:125℃,168 hr |
% | ISO 188 | |
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ISO 188 | |
TD:125℃,1008 hr TD:125℃,1008 hr |
% | ISO 188 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 6 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 7 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 8 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 7 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 6 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 8 |
ISO 188 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 类型 1 |
6 5 sec |
7 1 sec |
8 15 sec |
【新闻资讯】查看全部
车辆结构:增强塑料卷带
2017-06-21 车辆建设需要新的方法。虽然到目前为止的车辆大多是用铝和钢等金属制造的,但电动汽车的即将到来的时代将需要轻量化的建设。这意味着必须找到新的材料。纤维增强塑料具有显着 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |