牌号简介 About |
---|
生产高强度、韧性、功能性部件热塑性材料,提供最佳的机械性能。植物蓖麻油的可再生原料(减少对环境的影响)。提供优异的耐化学性和增强的断裂延伸率。用于假肢、鞋垫、运动用品、卡口配合、活铰链等的抗冲击性和延展性。质量以最低的成本每部分实现最低的成本每部分1和降低您的总拥有成本。尽量减少浪费-分批重复使用多余的粉末,获得功能部件,不再丢弃。获得一致的性能,同时实现70%的剩余粉末可重用性。优化成本和零件质量-成本效益高的材料和行业领先的剩余粉末可重用性。专为HP多喷嘴融合技术而设计,用于生产各种行业的功能部件和最终部件。在性能和可重用性之间提供最佳平衡。易于加工的材料使生产效率高,浪费少,成本低。设计用于可靠地生产最终零件和功能原型,具有精细的细节和尺寸精度。 Produce strong, ductile, functional parts Thermoplastic material delivering optimal mechanical properties. Renewable raw material from vegetable castor oil (reduced environmental impact). Provides excellent chemical resistance and enhanced elongation-at-break. Impact resistance and ductility for prostheses, insoles, sports goods, snap fits, living hinges, and more. Quality at the lowest cost per part Achieve the lowest cost per part1 and reduce your total cost of ownership. Minimize waste - reuse surplus powder batch after batch and get functional parts, no throwing away anymore. Get consistent performance while achieving 70% surplus powder reusability. Optimize cost and part quality - cost-efficient material with industry-leading surplus powder reusability. Engineered for HP Multi Jet Fusion technology Designed for production of functional and final parts across a variety of industries. Provides the best balance between performance and reusability. Easy-to-process material enables high productivity, less waste, and lower cost. Engineered to reliably produce final parts and functional prototypes with fine detail, dimensional accuracy. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.04 | g/cm³ | ASTM D792 |
表观密度 Apparent density 3 |
0.48 | g/cm³ | ASTM D1895 |
颗粒大小 Particle size |
50.0 | µm | ASTM D3451 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 4 |
|||
XY 方向 XY direction |
1800 | MPa | |
ZX 方向 ZX direction |
1800 | MPa | |
拉伸强度 tensile strength 4 |
|||
XY 方向,断裂 XY direction, fracture |
MPa | ||
ZX 方向,断裂 ZX direction, fracture |
MPa | ||
拉伸应变 Tensile strain 4 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
|||
XY 方向 XY direction |
MPa | ||
ZX 方向 ZX direction |
MPa | ||
弯曲强度 bending strength 5 |
|||
XY 方向,5% 应变 XY direction, 5% strain |
MPa | ||
ZX 方向,5% 应变 ZX direction, 5% strain |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
kJ/m² | ASTM D256-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
ZX 方向:0.45 MPa,未退火 ZX direction: 0.45 MPa, unannealed |
℃ | ||
ZX 方向:1.8 MPa,未退火 ZX direction: 1.8 MPa, unannealed |
℃ | ||
熔融温度 Melting temperature 3 |
|||
DSC DSC 3 |
℃ | ASTM D3418 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Recyclability(Refresh ratio for stable performance) Recyclability(Refresh ratio for stable performance) |
% |
备注 |
---|
2. of parts |
3. Powder |
4. 类型 5, 50 mm/min |
5. 14 mm/min |
【新闻资讯】查看全部
【干货】注塑模具保护与维修时,应注意些什么?
2020-12-18 搜料网资讯: 注塑模具,作为注塑工厂最为主要的生产工具,它决定了产品的形状、规格、尺寸和外观光洁度。模具的材料为钢材,一般由前模和后模组成。 1.模具的保护 由于模具具有 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |