公司信息及水印
牌号简介 About |
---|
特点和优点组成:偏氟乙烯和六氟丙烯的二元聚合物中粘度工艺目标:注射、传递成型和压延与低氟聚合物相比提高了耐化学性与优良的压缩永久变形性与低氟聚合物的性能瑞公司固化技术 Features and Benefits Composition: di-polymer of vinylidene fluoride and hexafluoropropylene Medium viscosity Process targets: injection and transfer molding and calendering Improved chemical resistance compared to lower percent fluorine fluoropolymers Excellent compression set resistance compared to lower percent fluorine fluoropolymers Proprietary incorporated cure technology |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.85 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
37 | MU | |
氟含量 Fluorine content |
69 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
77 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
15.2 | MPa | |
100% 应变 100% strain |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
压缩形变 Compression deformation |
|||
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
MH(177℃) MH(177℃) |
J | ||
ML(177℃) ML(177℃) |
J | ||
t'50(177℃) t'50(177℃) |
min | ||
t'90(177℃) t'90(177℃) |
min | ||
ts2(177℃) ts2(177℃) |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Tr10 Tr10 |
℃ | ASTM D1329 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
2022年科思创杯“画出你的梦想,说出你的畅想”学生绘画及演讲比赛开
2022-04-20 围绕联合国可持续发展目标 肩负社会责任,助力优质教育 日前,由世界可持续发展领导力组织(World Organization for Sustainability Leadership,简称WOSL)主办、沃搜(上海)教育科技有限公司 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |