| 牌号简介 About |
|---|
| Vydyne® 840F是一种PA66基共聚物，具有高熔融强度、剪切稀化行为、高拉伸强度、延展性和慢结晶性，与乙烯的结晶温度/速率非常接近。Vydyne® 840F所展示的性能组合使其成为许多应用的很好的候选者，例如许多薄膜用途、片材和单丝。缓慢的结晶行为加上~215-220°C的熔点和良好的机械性能，使该材料非常适用于多层膜的外层或内层。这种材料还表现出非常高的断裂延伸率（>500%），允许热成型或薄膜定向时的高拉伸比。 Vydyne 840F is a PA66-based copolymer that features high melt strength, shear thinning behavior, high tensile strength, ductility, and slow crystallinity that matches crystallization temperatures/rates very close to that of ethylenes. The combination of properties exhibited by Vydyne 840F make it a good candidate for a number of applications such as numerous film uses, sheeting, and monofilament. The slow crystallization behavior coupled with the melting point ~ 215-220°C and great mechanical properties makes this material extremely useful for outside layers or internal layers of the multilayer film. This material further exhibits a very high elongation to break (> 500%) allowing for high draw ratios for thermoforming or when orienting the film. |
产品描述 Product Description
用途：多层薄膜;片材;棒材;工业应用;型材;单丝;真空袋薄膜;管件;
加工条件：挤出 Extrusion
性能特点： 熔体强度好; 机械强度好; 熔体稳定性高; 耐化学性; 韧性好; 抗穿孔性; Good Rigidity,Good flexibility,Good melt strength,Solvent resistance,Puncture Resistant,Higher melt stability
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.14 | g/cm³ | |
|
含水量 water content |
0.10 | % | |
|
体积密度 bulk density |
674 | g/l | |
|
相对粘度 Relative viscosity |
|||
|
（Formic Acid） （Formic Acid） |
115 到 145 | ||
|
（Sulphuric Acid） （Sulphuric Acid） |
3.80 到 4.10 | ||
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
膜刺穿力 Membrane puncture force |
|||
|
25 µm，Biaxially Oriented Film 25 µm，Biaxially Oriented Film |
N | ||
|
割线模量 Secant modulus |
|||
|
MD：25 µm，Biaxially Oriented Film MD：25 µm，Biaxially Oriented Film |
MPa | ||
|
MD：38 µm，铸造薄膜 MD: 38 µ m, cast thin film |
MPa | ||
|
TD：25 µm，Biaxially Oriented Film TD：25 µm，Biaxially Oriented Film |
MPa | ||
|
TD：38 µm，铸造薄膜 TD: 38 µ m, cast thin film |
MPa | ||
|
拉伸强度 tensile strength |
|||
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ||
|
MD，断裂，38 µm，吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ||
|
TD，断裂，38 µm，吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
MD，断裂，25 µm，双轴取向薄膜 MD, fracture, 25 µ m, biaxial oriented thin film |
% | ||
|
MD，断裂，38 µm，挤塑薄膜 MD, fracture, 38 µ m, extruded film |
% | ||
|
TD，断裂，25 µm，双向拉伸薄膜 TD, fracture, 25 µ m, biaxially stretched film |
% | ||
|
TD，断裂，38 µm，挤塑薄膜 TD, fracture, 38 µ m, extruded film |
% | ||
|
落锤冲击 Drop hammer impact |
|||
|
38 µm，铸造薄膜 38 µ m, cast thin film |
g | ||
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
MD：38 µm，铸造薄膜 MD: 38 µ m, cast thin film |
g | ||
|
TD：38 µm，铸造薄膜 TD: 38 µ m, cast thin film |
g | ||
|
自由收缩 Free contraction |
|||
|
MD，160℃，Biaxially Oriented Film MD，160℃，Biaxially Oriented Film |
% | ||
|
TD，160℃，Biaxially Oriented Film TD，160℃，Biaxially Oriented Film |
% | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔融温度 Melting temperature |
℃ | ||
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部 
陕西化企驰援河南抢险救灾
2021-08-09 搜料网资讯： 8月5日，国家危险化学品应急救援长庆油田队完成河南应急救灾任务返回西安，受到热烈欢迎，该公司执行董事、党委书记何江川为他们授予模范队旗帜并颁发《嘉奖令》 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付