| 牌号简介 About |
|---|
| ADSINT PA11天然，一种生物基材料（蓖麻油），是一种有趣的PA12替代品。最终产品具有较高的断裂延伸率、弹性和抗冲击性。典型应用是在具有高机械应力（如铰链）和特殊环境（如化学、清洁剂、油）的环境中。由于其延展性高，在碰撞情况下不会碎裂。它经过医学和食品应用认证。ADSINT PA11已经在最常见的SLS打印机上进行了测试。将提供打印参数。它也有黑色的。刷新率在35%-50%之间，具体取决于应用程序。 AdSint® PA11 natural, a bio-based material (castor oil), is an interesting alternative to PA12. The end product offers a high elongation at break, elasticity and high impact resistance. Typical applications are in environments with high mechanical stress (e.g. hinges) and special surroundings (e.g. chemical, detergents, oil). Due to its high ductility, it does not splinter in crash situations. It is certified for medical and food applications. AdSint® PA11 has been tested on most common SLS printers. Parameters for printing will be provided. It is also available in black. The refresh rate is between 35% - 50%, depending on the application. |
产品描述 Product Description
用途：医疗/护理用品;非特定食品应用;Additive Manufacturing (3D Printing);
加工条件：3D Printing, Laser Sintering/Melting 3D Printing, Laser Sintering/Melting
性能特点： 拉伸性能好; 可回收; 机械强度好-延展; 弯曲性能好; 冲击性能好; High impact resistance,Ductility,High elastic,Renewable resources,Good Tensile Strength
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.950 到 1.05 | g/cm³ | ISO 61 |
|
表观密度 Apparent density 2 |
0.48 到 0.58 | g/cm³ | ISO 1068 |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
0.90 到 1.1 | % | ISO 62 |
|
颗粒大小分布 Particle size distribution |
|||
|
Course Particles <15 µm Course Particles <15 µm |
< 10 | % | |
|
Course Particles >76 µm Course Particles >76 µm |
< 10 | % | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
玻璃化转变温度 Glass transition temperature 3 |
℃ | ISO 11357-2 | |
|
熔融温度 Melting temperature |
|||
|
-- -- 4 |
℃ | ||
|
-- -- 5 |
℃ | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Mean Diameter Mean Diameter |
µm | ISO 13320 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，20℃ Shore D, 20 ℃ |
ISO 868 | ||
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1B | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/1B | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/1B | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
| 备注 |
|---|
| 2. Packed |
| 3. Sintered Part |
| 4. Part |
| 5. Powder |
|
【新闻资讯】查看全部
脑洞大开！飞机内饰竟然可以这样3D打印出来！
2017-07-13 总部位于中国香港的Western Tool & Mold (WTM)服务于航空航天内饰市场，在该市场中，航空公司需要快速更换零件来提高供应链效率，但由于个别组件的几何形状很独特，这种需求往往很难得到满足。 Western Tool & Mold目前正在使用Stratasys 3D打印技术来打印具有复杂外形和少量需求的飞机零件，如头等舱头顶行李箱储物柜和卫生间组件。通过直接使用CAD设计3D打印这些零件，省略金属制造流程，WTM的客户可以在设计过程的早期测试零 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付