Sarlink® TPV 24464是一种通用热塑性硫化剂,用于汽车和工业应用。Sarlink® TPV 24464是一种中等硬度、低密度、符合RoHS标准的等级,适用于注塑和挤出。 Sarlink TPV 24464 is a general purpose thermoplastic vulcanizate used in automotive and industrial applications. Sarlink TPV 24464 is a medium hardness, low density, RoHS compliant grade suitable for injection molding and extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,1 秒,注塑成型 Shore A, 1 second, injection molding |
69 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
66 | ||
邵氏 A,15 秒,注塑成型 Shore A, 15 seconds, injection molding |
65 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
TD,断裂 TD, fracture |
MPa | ||
MD,断裂 MD, fracture |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
TD,断裂 TD, fracture |
% | ||
流量,断裂 Flow rate, fracture |
% | ||
撕裂强度 tear strength 3 |
|||
TD TD |
kN/m | ||
MD MD |
kN/m | ||
压缩形变 Compression deformation 4 |
|||
23℃,22 hr 23℃,22 hr |
% | ||
70℃,22 hr 70℃,22 hr |
% | ||
90℃,70 hr 90℃,70 hr |
% | ||
125℃,70 hr 125℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
|||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ||
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ||
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ||
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ||
TD:125℃,168 hr TD:125℃,168 hr |
% | ||
MD:125℃,168 hr MD:125℃,168 hr |
% | ||
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ||
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ||
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
|||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ||
流量:110℃,1008 hr Flow rate: 110 ℃, 1008 hr |
% | ||
TD:125℃,168 hr TD:125℃,168 hr |
% | ||
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 6 |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 7 |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 8 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 6 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 7 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 8 |
|||
法律声明 Legal Statement |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
|||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,100% 应变 TD, 100% strain |
2.03 | MPa | |
MD,100% 应变 MD, 100% strain |
3.45 | MPa |
备注 |
---|
2、类型 1, 510 mm/min |
3、B 方法,直角形试样(不割口), 510 mm/min |
4、类型 A |
5、类型 1 |
6、1 sec |
7、5 sec |
8、15 sec |
【新闻资讯】查看全部
模具从设计到消费成品,扒一扒每一步...
2017-01-03 模具设计大型产品研发过程中的一个重要环节。由于产品和模具设计是相互依存的,因此了解塑料零件的开发过程、模具设计过程及模具制造过程的作用对产品设计工程师和模具设计工程师来说是非常有用的。典型的产品开发过程不同阶段,包括:产品定义、产品设计、经验和产品开发、提升产能、投放市场。 尽管产品开发流程复杂,但多数具有以下两个关键属性: 1.建立系统性开发计划 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |