牌号简介 About |
---|
BC8870是一种低粘度双组分聚氨酯浇注料,专门为高耐磨性和抗冲击性而配制。推荐用于生产高耐磨零件和衬里的铸件。本产品是一种安全、易于操作、室温混合和固化系统,不含TDI、MDI或MOCA。BC8870对典型的环境湿度相对不敏感,可以制造出良好的无空隙零件,而不会出现一些传统聚氨酯系统所显示的问题。 BC8870 is a low viscosity two-component urethane casting compound that is specifically formulated for high abrasion and impact resistance. It is recommended for use for the production casting of highly wear-resistant parts and linings. This product is a safe, easy-to-handle, room temperature mixing and curing system that does not contain TDI, MDI, or MOCA. BC8870 is relatively insensitive to typical environmental moisture and will make good void-free parts without the problems hat some conventional urethane systems exhibit. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | |
收缩率 Shrinkage rate |
|||
MD MD |
0.25 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脱模时间 stripping time |
|||
24℃ 24℃ |
120 到 180 | min | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 2 |
|||
-- -- 3 |
Clear/Transparent | ||
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
100 | ||
Part B Part B |
|||
粘度 viscosity 4 |
|||
24℃ 24℃ 4 |
Pa·s | ||
固化时间 Curing time |
|||
24℃ 24℃ |
hr | ||
储存稳定性 storage stability |
|||
24 ℃ 24 ℃ |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
拉伸模量 Tensile modulus |
MPa | ||
拉伸强度 tensile strength |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ||
压缩形变 Compression deformation |
|||
Method B Method B |
% | ASTM D395 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
回弹性 Resilience |
% | ASTM D575 |
备注 |
---|
2、Part B |
3、Part A |
4、Mixed |
【新闻资讯】查看全部
注塑机开合模控制需要留意的成绩
2017-12-14 开模控制: 当熔融塑料注射入模腔内及至冷却完成后,随着便是开模动作,取出制品。开模过程也分三个阶段。第一阶段慢速开模,防止制件在模腔内撕裂。 第二阶段快速开模,以缩短开模时间。第三阶段慢速开模,以减低开模惯性造成的冲击及振动。 合模控制: |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |