牌号简介 About |
---|
ELTEX PF6180AA是一种高流动性的聚乙烯,适用于挤出涂层、铸膜挤出、注塑以及化合物和母料应用。ELTEX PF6180AA是一种用茂金属催化剂制备的以己烯-1为共聚单体的聚乙烯共聚物。ELTEX PF6180AA具有以下特性:优越的密封性能优异的机械性能挤出涂层聚合物的应用对于要求很高的密封应用,对于铸膜挤出聚合物的机械性能对铸膜拉伸膜的表皮层有好处。用于注射成型聚合物的表面光洁度方面,适用于要求较高刚度/韧性平衡的注射零件、具有优异抗ESCR性能的母粒和具有基本添加剂包装的化合物聚合物、母粒和化合物的载体树脂、高填充水平的化合物。 ELTEX® PF6180AA is a polyethylene of high fluidity suitable for extrusion coating, cast film extrusion, injection moulding as well as compounds and masterbatches applications. Benefits & Features ELTEX® PF6180AA is a polyethylene copolymer containing hexene-1 as comonomer produced with a metallocene catalyst. ELTEX® PF6180AA offers the following properties: Superior sealing performance Outstanding mechanical properties Applications For extrusion coating Extrusion coating polymer for highly demanding applications regarding sealing and mechanical properties For cast film extrusion Polymer for the skin layers of cast stretch film to the benefit of enhanced surface finish aspect For injection moulding Polymer for injected parts requiring superior stiffness/toughness balance Excellent ESCR resistance Outstanding impact properties For masterbatch and compounds Polymer with basic additive package, for carrier resin of masterbatches and compounds High level of fillers |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.916 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
8.0 | g/10min | ISO 1133 |
全切口蠕变试验 Full incision creep test 2 |
|||
40℃ 40℃ 2 |
> 1.1 | month | ISO 16770 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-20℃,局部断裂 -20 ℃, localized fracture |
88 | kJ/m² | ISO 180-A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
97.0 | ℃ | ISO 306/A50 |
熔融温度 Melting temperature 3 |
℃ | ISO 11357-3 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
2、3 MPa, 2% Arkopal N100 |
3、DSC 2nd heating, 10°C/min |
【新闻资讯】查看全部
科亚装备集团:SK96型双螺杆一步挤出片材生产线用户验收投产!
2021-03-19 搜料网资讯: 2020年12月,南京科亚某欧洲用户越南工厂TPU改性一步法片材挤出生产线正式验收投产!疫情期间,科亚工程师不辞辛苦亲自奔赴越南工厂指导生产线的安装与调试。在科亚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |