| 牌号简介 About |
|---|
| Ingeo™ 3D870是为制造3D打印机单丝而开发的一个等级。设计用于向3D打印部件提供改进的耐热性和高冲击强度，该配方等级可实现类似于ABS的热性能和机械性能，同时提供了替代苯乙烯基材料的方案。由Ingeo™ 3D870制成的单丝具有良好的3D打印特性，如精确的细节、良好的粘合性、较少的翘曲或卷曲以及低气味。 Ingeo 3D870 is a grade developed for manufacturing 3D printer monofilament. Engineered to deliver improved heat-resistance and high impact strength to 3D printed parts, this formulated grade achieves thermal and mechanical properties similar to ABS while offering an alternative to styrenic-based materials. Monofilaments made with Ingeo 3D870 provide excellent 3D printing characteristics such as precise detail, good adhesion to build plates, less warping or curling, and low odor. |
产品描述 Product Description
用途：单丝;细丝;
加工条件：3D Printing, Fused Filament Fabrication (FFF)
性能特点： 耐热性好; 可回收; 可堆肥; 低VOC; 粘结性好; 低翘曲性; 冲击性能好; Low warping,High impact resistance,Renewable resources,Low odor,Good bond,Compostable,Heat Resistance, Good
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.22 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
210℃，2.16kg 210℃，2.16kg |
9.0 到 15 | g/10min | ASTM D1238 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
-- -- 2 |
2870 | MPa | |
|
-- -- 3 |
2450 | MPa | |
|
-- -- 4 |
2480 | MPa | |
|
拉伸强度 tensile strength |
|||
|
-- -- 2 |
MPa | ||
|
-- -- 3 |
MPa | ||
|
-- -- 4 |
MPa | ||
|
弯曲模量 Bending modulus |
|||
|
-- -- 2 |
MPa | ||
|
-- -- 3 |
MPa | ||
|
-- -- 4 |
MPa | ||
|
弯曲强度 bending strength |
|||
|
-- -- 2 |
MPa | ||
|
-- -- 3 |
MPa | ||
|
-- -- 4 |
MPa | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-- -- 5 |
J/m | ||
|
-- -- 6 |
J/m | ||
|
-- -- 7 |
J/m | ||
|
-- -- 8 |
J/m | ||
|
-- -- 9 |
J/m | ||
|
-- -- 10 |
J/m | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 11 |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed 11 |
℃ | ASTM E2092 | |
|
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
|
|||
| 备注 |
|---|
| 2、XY Axis, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 3、YX Axis, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 4、ZX Axis, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 5、XY Axis, Amorphous, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 6、YX Axis, Amorphous, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 7、ZX Axis, Amorphous, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 8、XY Axis, Crystalline, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 9、YX Axis, Crystalline, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 10、ZX Axis, Crystalline, 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 11、3D printed part, 100% in-fill, annealed at 110°C/15 min |
|
【新闻资讯】查看全部
巴陵石化试用国产羟胺过滤器滤芯成功
2016-01-13 1月11日从巴陵石化己内酰胺事业部获悉，该部羟胺肟化车间试用国产化羟胺不对称金属薄膜烧结滤芯取得成功，至今已连续运行1个多月。该滤芯的国产化不仅可降低生产成本，还将填补我国在这一领域工业应用的空白，促进采购优化。 据介绍，一直以来，己内酰胺事业部的羟胺过滤器绝大部分使用的是德国产滤芯。为打破这一局面，该事业部于2014年对国产不锈钢烧结金属滤芯进行样品选型，当年11月份开展为期10天的工业化试用。此后，攻关团队查找初次试用未果的原因，与产家一起优化改进。2015年10月初， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付