牌号简介 About |
---|
CLEAR COTE Captain's Club树脂是一种低剖面、低收缩、不饱和聚酯树脂,设计用于室温固化,并添加一种MEK过氧化物催化剂。该系统具有良好的玻璃湿,不排水。该系统具有适度的凝胶时间和快速固化,具有良好的修整时间,允许固化为刚性固体,保持优异的韧性和强度。该树脂适用于船舶/造船应用、零件生产和其他一般用途。 CLEAR COTE™ Captain's Club resin is a low profile, low shrinkage, unsaturated polyester resin designed for room temperature curing, with the addition of an MEK Peroxide catalyst. This system features excellent glass wet out without draining. This system has a Moderate gel time and fast cure with a good trim time that allows for cures to a rigid solid, maintaining excellent toughness and strength. This resin is suitable for marine/boat-building applications, parts production, and other general purpose uses. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
结合苯乙烯 Combined with styrene |
< 35.0 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
按重量计算的混合比: 100 | ||
部件 B Component B |
按重量计算的混合比: 1.0 | ||
贮藏期限 Storage period |
< 17 | wk | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
9.0 到 14.0 | min | |
放热峰值 exothermic peak |
℃ | ||
触变指数 Thixotropic index |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
-- -- 1 |
Pa·s | ||
-- -- 2 |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 at 60rpm |
3 at 6rpm |
【新闻资讯】查看全部
三角冬季轮胎高铁品牌专列,北京北站启程!
2021-10-23 搜料网资讯: 10月20日上午,三角冬季轮胎高铁品牌专列首发仪式在北京北站举行。 三角集团有限公司党委副书记魏楠、华铁传媒集团董事长路立明为首发仪式揭幕。三角冬季轮胎登陆 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Clear Cote™ CAPTAIN'S CLUB BOATYARD RESIN证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)