牌号简介 About |
---|
CALIBRE™ 2060-3聚碳酸酯树脂用于涉及蒸汽或环氧乙烷灭菌的医疗应用中,尽管其适用性取决于高压釜循环时间和温度。CALIBRE™ 2060-3具有特殊的清晰度、耐热性、冲击强度和低污染水平。Calibre 2000系列树脂已根据ISO 10993-1(医疗器械生物学评估)进行了评估,并适用于批准的医疗应用。根据ISO 10993 FDA 21 CFR 177.1580抗脂质应用医学应用注射或挤压应用测试的主要特性 CALIBRE™ 2060-3 Polycarbonate resin is used in medical applications involving steam or ethylene oxide sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and temperatures. CALIBRE 2060-3 provides exceptional clarity, heat resistance, impact strength and has low contamination levels. The CALIBRE 2000 series of resins have been evaluated with respect to ISO 10993-1 (Biological Evaluation of Medical Devices) and are suitable for use in approved medical applications. Main Characteristics Tested under ISO 10993 FDA 21 CFR 177.1580 Lipid resistance Applications Medical application Injection or extrusion applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
3.5 | g/10min | ASTM D1238 |
300℃,1.20kg 300℃,1.20kg |
3.5 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
ASTM D256 | ||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance 7 |
|||
3180 µm 3180 µm 7 |
% | ASTM D1003 | |
雾度 Haze 7 |
|||
3180 µm 3180 µm 7 |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
% | ASTM D1044 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
2 一般属性:这些不能被视为规格。 |
3 2.0 in/min |
4 方法 I (三点负荷), 0.079 in/min |
5 0.079 in/min |
6 速率 A (50°C/h), 载荷2 (50N) |
7 1/8 inch thickness plaque |
【新闻资讯】查看全部
将来聚氨酯资料应用率将达保温资料50%
2016-11-11 在中国聚氨酯工业协会制定的发展规划中,五年后聚氨酯材料应用率将达到保温材料的50%左右。“但是目前中国的市场占有率不到10%,而国外保温材料市场中聚氨酯的的份额很大,美国达到57%,日本达32%。”在中国聚氨酯绿色节能华东地区高峰论坛上,杨宗�j聚氨酯高科技新材料研发专家团队的成员如是分析。 聚氨酯是当代最佳节能保温材料,因其使用寿命长、保温效果好、耐温性能强以及节能环保而被普遍应用于建筑保温以及建筑防火等领域,在建筑保温材料市场中占据相当大的份额。 但是, |
将来聚氨酯资料应用率将达保温资料50% 在中国聚氨酯行业协会制订的建设规划中,五年后聚氨酯原材料使用率将做到保温材料的50%上下。“可是现阶段中国的市场份额不上10%,而海外保温材料销售市场中聚氨酯的的市场份额非常大,英国做到57%,日本达32%。”在中国聚氨酯翠绿色环保节能华东区峰会上,杨宗�j聚氨酯新科技新型材料产品研发专家团的组员如果是剖析。 聚氨酯是当今最好环保节能保温材料,因其使用期限长、隔热保温效果非常的好、耐高温性能强及其绿色环保而被广泛运用于墙体保温及其建筑防火规范等行业,在工程建筑保温材料销售市场中占有非常大的市场份额。 可是,现阶段出現了一个让人难堪的难题,便是与一样是保温材料的聚苯保温板对比,其出厂价要高过聚苯保温板。以B1级保温材料测算,聚氨酯保温原材料是1800元/平米,而XPS是650元/平米,EPS是550元/平米。再再加上领域內外出現的恶性价格竞争,造成 聚氨酯在中国保温材料市场份额不上10%。 现阶段,在我国的保温材料销售市场关键以聚氨酯发泡EPS和XPS等为主导,大部分商品制造商根据在原料中加上无卤阻燃剂来提升保温材料的防火安全性能。在其中,生产制造所述保温材料的关键原材料是六溴环十二烷,一种在绝缘层、纺织品和电子器件行业常见的无卤阻燃剂。但2013年5月,联合国组织《关于持久性有机污染物的斯德哥尔摩公约》网络投票一致根据一项限令:在全世界范畴内严禁生产制造和应用六溴环十二烷。 六溴环十二烷是一种高溴成分的脂环族加上型无卤阻燃剂,现阶段关键用以EPS聚氨酯发泡聚乙烯,聚丙稀、环氧树脂胶、有机硅树脂和其他苯乙烯树脂中。但另外,他们也可以长期地存有于自然环境中,并在生物组织中堆积,对身体健康很有可能的危害。中国阻燃性学好副理事长、北京工商大学副教授职称钱立军表明,HBCD是一种新式的持续性有机空气污染物,是墙体保温材料中的隐形杀手,具备致癌物质、胎儿畸形等不良影响。 在参会的诸多权威专家来看,聚氨酯不但具备优良的隔热、阻燃性、隔音降噪作用,也有翠绿色、环境保护、环保节能等作用,是现阶段销售市场上危害保温材料的最好代替品。特别是在现行政策对有机保温材料放开后,聚氨酯的发展趋势更进到一个迅速环节。 2010年上海大火以后,2011年3月4日,国家公安部公布了《关于进一步明确民用建筑外保温材料消防监督管理有关要求的通知》,要求了工业建筑外保温材料选用点燃性能为A级的原材料。 原中国聚氨酯研究室优点杨宗�j专家教授强调,墙体保温商品中有机原材料是达不上A级,而做为有机原材料的聚氨酯不做复合型解决,数最多能做到B1级。这代表着,在“65号文”下,聚氨酯工程建筑保温材料没法墙上。 因为有机保温材料占有销售市场90%的市场占有率,假如严苛依照“65号文”实行,基本上沒有原材料能够 符合要求,因而,2012年12月3日,国家公安部撤消了“65号文”,为有机保温材料放开。 北京工程建筑科学院高级讲师工程师职称涂逢祥强调,聚氨酯综合性优点较为显著,如较为薄、隔热保温实际效果也很好,因而聚氨酯领域拥有 宽阔的市场前景。 现阶段,聚氨酯保温原材料已被我国工业生产和信息化管理部列入绿色建筑工程项目。社区论坛当场,全国各地权威专家以苏州市创新的一款有机无机物协作阻燃性聚氨酯保温板才为例子,就中国新式环境保护聚氨酯保温原材料的性能、行业现状和未来前景进行深入分析。 来源于:互联网技术 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- 心电图机器衔接器
- 2019-06-28 0
- CALIBRE™ 2060-3聚碳酸酯树脂用于涉及蒸汽或环氧乙烷灭菌的医疗应用中,尽管其适用性取决于高压釜循环时间和温度。CALIBRE™ 2060-3具有特殊的清晰度、耐热性、冲击强度和低污染水平
- 阅读全文
心电图机器衔接器
抱歉!暂无数据。