| 牌号简介 About |
|---|
| CALIBRE™ 2060-3聚碳酸酯树脂用于涉及蒸汽或环氧乙烷灭菌的医疗应用中，尽管其适用性取决于高压釜循环时间和温度。CALIBRE™ 2060-3具有特殊的清晰度、耐热性、冲击强度和低污染水平。Calibre 2000系列树脂已根据ISO 10993-1（医疗器械生物学评估）进行了评估，并适用于批准的医疗应用。根据ISO 10993 FDA 21 CFR 177.1580抗脂质应用医学应用注射或挤压应用测试的主要特性 CALIBRE™ 2060-3 Polycarbonate resin is used in medical applications involving steam or ethylene oxide sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and temperatures. CALIBRE 2060-3 provides exceptional clarity, heat resistance, impact strength and has low contamination levels. The CALIBRE 2000 series of resins have been evaluated with respect to ISO 10993-1 (Biological Evaluation of Medical Devices) and are suitable for use in approved medical applications. Main Characteristics Tested under ISO 10993 FDA 21 CFR 177.1580 Lipid resistance Applications Medical application Injection or extrusion applications |
产品描述 Product Description
用途：医疗/护理用品;
加工条件：注射成型 Injection Molding
性能特点： 蒸汽消毒; 高压灭菌器消毒; 耐高温; 透光性好; 冲击性能好; 环氧乙烷消毒; Good Clarity,High impact resistance,Steam sterilized,High pressure disinfection,High Heat Resistance,Ethylene oxide disinfection
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
3.5 | g/10min | ASTM D1238 |
|
300℃，1.20kg 300℃，1.20kg |
3.5 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.50 to 0.70 | % | ISO 294-4 |
|
MD MD |
% | ASTM D955 | |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
|
23℃，24hr 23℃，24hr |
% | ISO 62 | |
|
23℃，24hr 23℃，24hr |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
ASTM D256 | ||
|
23℃ 23℃ |
kJ/m² | ISO 180-A | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
ISO 180 | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
|
B50 B50 |
℃ | ISO 306 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~82℃ MD：-40~82℃ |
1/℃ | ASTM D696 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
折射率 Refractive index |
ISO 489 | ||
|
透光率 Transmittance 7 |
|||
|
3180 µm 3180 µm 7 |
% | ASTM D1003 | |
|
雾度 Haze 7 |
|||
|
3180 µm 3180 µm 7 |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 3 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 |
MPa | ISO 178 | |
|
泰伯耐磨性 Taber abraser |
% | ASTM D1044 | |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
| 2 一般属性：这些不能被视为规格。 |
| 3 2.0 in/min |
| 4 方法 I (三点负荷), 0.079 in/min |
| 5 0.079 in/min |
| 6 速率 A (50°C/h), 载荷2 (50N) |
| 7 1/8 inch thickness plaque |
|
【新闻资讯】查看全部 
西方石油建设低碳生物乙烯工厂
2021-05-07 搜料网资讯： 据烃加工网站5月3日报道 西方石油公司的低碳 部门周二表示，计划建设和运营一个试点工厂，使用人造二氧化碳（而 非碳氢化合物原料）生产生物乙烯。 该试验工厂将由 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付