| 牌号简介 About |
|---|
| Evoprene Cogee系列是专门为工程热塑性塑料（ETPS）提供共成型或共挤出材料而开发的。这使得，例如，聚酰胺（尼龙）手柄或ABS外壳能够获得一种Solt触摸感，而聚碳酸酯透镜可以有垫圈成型，以提供防风雨的产品。Evoprene Cogee等级是改性的Kraton G基化合物。Evoprene G和Evoprene Super G系列所显示的许多特征都由Evoprene Cogee化合物显示。然而，为了获得最佳的结合强度和性能特性，它们的处理方式必须完全不同。 The Evoprene COGEE range was specially developed to provide materials which will comould or coextrude to engineering thermoplastics (ETPs). This enables, for example, polyamide (nylon) handles or ABS housings to be given a solt touch feel whilst polycarbonate lenses can have gaskets moulded on to provide a weathertight product. The Evoprene COGEE grades are modified Kraton G based compounds. Many of the characteristics exhibited by the Evoprene G and Evoprene Super G ranges are shown by Evoprene COGEE compounds. However, they do have to be processed quite differently to obtain optimum bond strengths and performance characteristics. |
产品描述 Product Description
用途：柔软触感应用;
加工条件：注射成型 Injection Molding
性能特点： 耐臭氧; 耐候抗UV; Weather resistance is good,Ozone resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.07 | g/cm³ | ISO 2781 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
44 | ISO 868 | |
|
抗磨损性 abrasion resistance |
298 | mm³ | DIN 53516 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
2.70 | MPa | ISO 37 |
|
300% 应变 300% strain |
3.10 | MPa | ISO 37 |
|
100% 应变 100% strain |
MPa | ISO 37 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 37 | |
|
撕裂强度 tear strength 2 |
kN/m | ISO 34-1 | |
|
压缩形变 Compression deformation |
ISO 815 | ||
|
23℃，72 hr 23℃，72 hr |
% | ISO 815 | |
|
70℃，22 hr 70℃，22 hr |
% | ISO 815 | |
|
100℃，22 hr 100℃，22 hr |
% | ISO 815 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
使用温度 Operating temperature |
℃ | ||
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度的变化率 在空气中（125℃，336 hr） The rate of change in tensile strength in air (125 ℃, 336 hr) |
% | ISO 1817 | |
|
Change in Tensile Strain at Break in Air（125℃，336 hr） Change in Tensile Strain at Break in Air（125℃，336 hr） |
% | ISO 1817 | |
|
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
|
125℃，336 hr 125℃，336 hr |
ISO 1817 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Bond Strength Bond Strength |
MPa | Internal Method | |
|
M-S Flow M-S Flow |
MPa | Internal Method | |
|
耐臭氧性 Ozone resistance 3 |
|||
|
35℃ 35℃ 3 |
ISO 1431-1 | ||
|
UV Rating（40℃） UV Rating（40℃） 4 |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 B 方法，直角形试样（不割口） |
| 3 100 pphm/200 hrs/20% Strain |
| 4 350 hrs |
|
【新闻资讯】查看全部 
IEA：2050年石化品将占原油需求55%
2021-10-31 搜料网资讯： 近日，国际能源机构(IEA)表示，到2050年，交通、工业和住宅供暖的电气化将使石化行业成为原油的主要消费行业，占化石燃料需求的55%。 IEA在其《2021年全球能源展望》中 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付