| 牌号简介 About |
|---|
| PRE-ELEC® PS 1340是一种基于聚苯乙烯的导电热塑性浓缩物。导电性是通过使用高浓度的特殊导电炭黑来实现的。PRE-ELEC® PS 1340可使用未经处理或回收的聚苯乙烯稀释至60%。应始终测试实际量，因为它还取决于加工条件。典型应用包括用于热成型托盘的单或共挤片材。 PRE-ELEC® PS 1340 is a conductive thermoplastic concentrate based on polystyrene. Conductivity is achieved by using a high concentration of special conductive carbon black. PRE-ELEC® PS 1340 can be diluted up to 60% with virgin or recycled polystyrene. The actual amount should always be tested as it also depends on the processing conditions. Typical applications include mono- or co-extruded sheets for thermoformed trays. |
产品描述 Product Description
用途：片材;热成型应用;
加工条件：挤出 Extrusion
性能特点： 导电; Conductive
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.22 | g/cm³ | ASTM D792 |
|
密度 Density |
1.22 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
200℃，21.6kg 200℃，21.6kg |
1.2 | g/10min | ISO 1133 |
|
200℃，21.6kg 200℃，21.6kg |
1.2 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.40 to 0.60 | % | ASTM D955 |
|
MD MD |
% | ISO 294-4 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ISO 868 | ||
|
邵氏 A Shaw's A |
ISO 868 | ||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2 | |
|
屈服 yield |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
断裂 fracture |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2 | |
|
屈服 yield |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
-20℃ -20℃ 2 |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ 3 |
kJ/m² | ISO 179 | |
|
23℃ 23℃ 3 |
kJ/m² | ISO 179 | |
|
23℃ 23℃ 2 |
kJ/m² | ASTM D256 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 3 |
|||
|
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
ISO 179 | ||
|
23℃ 23℃ |
ASTM D256 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
ISO 180 | ||
|
Area Area |
ASTM D256 | ||
|
-20℃，4.00 mm -20℃，4.00 mm |
kJ/m² | ASTM D256 | |
|
23℃，4.00 mm 23℃，4.00 mm |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
|
-20℃，4 mm -20℃，4 mm |
kJ/m² | ASTM D256 | |
|
23℃，4 mm 23℃，4 mm |
ASTM D256 | ||
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 3 |
ISO 180 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
ISO 180 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 4 | |
|
-- -- |
℃ | ASTM D1525 5 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
B50 B50 |
℃ | ISO 306 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ESD STM11.11 | |
|
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
|
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 4 mm thickness |
| 3 4 mm thick |
| 4 标准 B (120°C/h), 载荷2 (50N) |
| 5 速率 A (50°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
Word天！塞拉尼斯要收购屹立？
2016-12-02 这两天，塑料行业流传着这样一条消息：塞拉尼斯(Celanese)要收购以色列尼龙纤维制造商屹立(Nilit)。 屹立在中国苏州的两家工厂，专注于生产锦纶6.6弹力丝和热塑性工程塑料< |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |