PS，PRE-ELEC® PS 1340对比PS，PRE-ELEC® PS 1324物性表,价格行情_搜料

牌号信息	PRE-ELEC® PS 1340 物性表 PS & 芬兰普宓斯指导价格：暂无塑料库存：缺货	PRE-ELEC® PS 1324 物性表 PS & 芬兰普宓斯指导价格：暂无塑料库存：缺货
牌号简介	PRE-ELEC® PS 1340是一种基于聚苯乙烯的导电热塑性浓缩物。导电性是通过使用高浓度的特殊导电炭黑来实现的。PRE-ELEC® PS 1340可使用未经处理或回收的聚苯乙烯稀释至60%。应始终测试实际量，因为它还取决于加工条件。典型应用包括用于热成型托盘的单或共挤片材。 PRE-ELEC® PS 1340 is a conductive thermoplastic concentrate based on polystyrene. Conductivity is achieved by using a high concentration of special conductive carbon black. PRE-ELEC® PS 1340 can be diluted up to 60% with virgin or recycled polystyrene. The actual amount should always be tested as it also depends on the processing conditions. Typical applications include mono- or co-extruded sheets for thermoformed trays.	PRE-ELEC® PS 1324是一种基于聚苯乙烯的碳黑填充导电热塑性化合物。除了低电阻率。PRE-ELEC® PS 1324具有良好的机械性能平衡，易于挤压。典型应用包括热成型静电放电托盘的挤压板。 PRE-ELEC® PS 1324 is a carbon black filled conductive thermoplastic compound based on polystyrene. In addition to a low electrical resistivity. PRE-ELEC® PS 1324 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include extruded sheet for thermoformed ESD trays.

产品描述
厂家：	芬兰普宓斯 Premix Oy	芬兰普宓斯 Premix Oy
类别：	PS PS	PS PS
填料：
用途：	热成型应用,片材
性能特点：	导电 Conductive	易加工,导电 Excellent Processability,Conductive
加工条件：	挤出 Extrusion	挤出 Extrusion

技术参数

物理性能
PHYSICAL PRE-ELEC® PS 1340 PRE-ELEC® PS 1324 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

熔体质量流动速率(200℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，21.6kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL PRE-ELEC® PS 1340 PRE-ELEC® PS 1324 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(4 mm)
Bending modulus MPa ASTM D790

弯曲模量(4 mm)
Bending modulus MPa ISO 178

拉伸应变(TD，屈服)
Tensile strain % ASTM D638

拉伸应变(TD，屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(流量，屈服)
Tensile strain % ASTM D638

拉伸应变(流量，屈服)
Tensile strain % ISO 527-2

拉伸应变(流量，断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ISO 527-2

拉伸强度(--)
tensile strength MPa ISO 527-2

拉伸强度(MD)
tensile strength MPa ASTM D638

拉伸强度(MD，屈服)
tensile strength MPa ASTM D638

拉伸强度(MD，屈服)
tensile strength MPa ISO 527-2

拉伸强度(TD)
tensile strength MPa ASTM D638

拉伸强度(TD，屈服)
tensile strength MPa ASTM D638

拉伸强度(TD，屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

邵氏硬度(邵氏 A)
Shore hardness ASTM D2240

邵氏硬度(邵氏 A)
Shore hardness ISO 868

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT PRE-ELEC® PS 1340 PRE-ELEC® PS 1324 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-20℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(-20℃，4 mm)
Notched impact strength of cantilever beam kJ/m² ASTM D256

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180

悬臂梁无缺口冲击强度(23℃，4 mm)
Notched impact strength of cantilever beam kJ/m² ASTM D256

悬臂梁无缺口冲击强度(23℃，4 mm)
Notched impact strength of cantilever beam ASTM D256

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-20℃，4.00 mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃，4.00 mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(Area)
Impact strength of cantilever beam notch ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL PRE-ELEC® PS 1340 PRE-ELEC® PS 1324 单位
UNIT 测试方法
TEST METHOD

Bending Test(--)
Bending Test Cycles

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-B

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-A

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 4

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 5

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL PRE-ELEC® PS 1340 PRE-ELEC® PS 1324 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

表面电阻率
Surface resistivity ohms ESD STM11.11

表面电阻率
Surface resistivity ohms IEC 61340-2-3

加工方式

挤出 PRE-ELEC® PS 1340 PRE-ELEC® PS 1324 单位测试方法

干燥时间 hr

干燥温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒5区温度 °C

备注

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 4 mm thick

4 标准 B (120°C/h), 载荷2 (50N)

5 速率 A (50°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 Across Flow

3 Flow

4 4 mm thickness

5 速率 A (50°C/h), 载荷2 (50N)

6 Across Flow, ISO 5626

7 Flow, ISO 5626


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
挤出
备注
返回顶部