ELITE™ AT 6111增强聚乙烯树脂是一种乙烯-辛烯共聚物的基础上的精英AT技术从陶氏。该树脂专为托盘包装应用中的铸造拉伸机械包装膜而设计,并提供了延展性、冲击强度和抗穿刺性的最佳平衡。主要特点:良好的延展性、高冲击性和优异的抗穿刺性、低背压和低功耗的优良加工性。符合:美国食品和药物管理局FCN 424欧盟,第10/2011号加拿大HPFB。无异议。有关完整的详细信息,请咨询法规。 ELITE™ AT 6111 Enhanced Polyethylene Resin is an ethylene-octene copolymer based on ELITE™ AT technology from Dow. This resin is designed for cast stretch machine wrap films in pallet wrap application and offers an optimized balance of extensibility, impact strength, and puncture resistance. Main Characteristics: Excellent extensibility High impact and exceptional puncture resistance Excellent processibility with low back pressure and power consumption. Complies with: U.S. FDA FCN 424 EU, No 10/2011 Canadian HPFB No Objection Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.912 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.7 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
20 µm 20 µm |
2.87 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
|||
20 µm 20 µm |
36.9 | N | 内部方法 |
膜耐刺穿性 Membrane puncture resistance |
|||
20 µm 20 µm |
J/cm³ | 内部方法 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,20 µm MD, yield, 20 µ m |
MPa | ASTM D882 | |
TD,屈服,20 µm TD, yield, 20 µ m |
MPa | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
20 µm 20 µm |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
MD:20 µm MD:20 µm |
g | ASTM D1922 | |
TD:20 µm TD:20 µm |
g | ASTM D1922 | |
最终拉伸 Final stretching 3 |
|||
OnPallet Testing,20.3 µm OnPallet Testing,20.3 µm 3 |
% | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20.3 µm 45°,20.3 µm |
ASTM D2457 | ||
雾度 Haze |
|||
20.3 µm 20.3 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Method B |
3 Determined by Highlight Industries, Inc. |
【新闻资讯】查看全部
ABS注塑件怎么才干添加光亮度
2019-01-29 在注塑生产中,塑件光泽不良的主要是:模具、注塑工艺、原料这三方面的原因。以下就此问题作如下简述,欢迎指正评论! 一、注塑模具 1.模具型腔加工不良 如模具型腔有伤痕、微孔 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |