牌号简介 About |
---|
JM-365是高抗冲嵌段共聚物,具有较高的乙丙橡胶含量。该等级设计用于在常规注射成型设备中加工。与普通嵌段共聚物相比,JM-365具有较好的抗冲击性能,并具有良好的物理性能平衡。 Description JM-365 is high impact block copolymer which has high ethylene-propylene rubber content. This grade is designed to be processed in conventional Injection molding equipment. JM-365 shows better impact resistance than normal block opolymer and has good physical property balance. Applications Industrial supplies Automotive compound base resin |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
26 | g/10min | ASTM D1238,ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
25.5 | MPa | ASTM D638 |
屈服 yield |
25.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 50 | % | ASTM D638 |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-10℃ -10℃ |
J/m | ASTM D256 | |
-10℃ -10℃ |
J/m | ISO 180 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
金发科技Vs巴斯夫,透过专利纠纷,看两大化工公司的生物降解材料市场
2021-03-03 搜料网资讯: 近日,国家知识产权局下发《无效宣告请求审查决定书》(第48147号),裁定巴斯夫名称为连续生产可生物解聚酯的方法的专利权部分无效,但同时决定在巴斯夫于2020年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |