牌号简介 About |
---|
3M Dyneon TFM改性聚四氟乙烯化合物TFM 6302是基于第二代改性悬浮聚四氟乙烯(含10%石墨)的自由流动化合物,用于冲压、压缩和自动成型。特殊特性增加了热尺寸稳定性增加了表面硬度改善了负载下的变形减少了摩擦和磨损良好的化学稳定性高极限氧指数(LOI)低摩擦性能非常好的机械性能优异的耐温性 Texin 950 resin is an aromatic polyether-based thermoplastic polyurethane with a Shore hardness of approximately 50D. It can be processed by injection molding, extrusion, or blow molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ASTM D792 , ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:2.54 mm MD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
0.80 | % | ISO 2577 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 , ISO 37 | ||
屈服 yield |
MPa | ASTM D412 , ISO 37 | |
50% 应变 50% strain |
MPa | ASTM D412 , ISO 37 | |
100% 应变 100% strain |
MPa | ASTM D412 , ISO 37 | |
300% 应变 300% strain |
MPa | ASTM D412 , ISO 37 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412,ISO 37 | |
撕裂强度 tear strength |
|||
-- -- 2 |
kN/m | ASTM D624 | |
-- -- |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B , ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B,ISO 815 | |
23℃,22 hr 23℃,22 hr 3 |
% | ASTM D395B,ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B,ISO 815 | |
70℃,22 hr 70℃,22 hr 3 |
% | ASTM D395B,ISO 815 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,100℃,70 hr 100% strain, 100 ℃, 70 hr |
% | ASTM D573 | |
300% 应变,100℃,70 hr 300% strain, 100 ℃, 70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,100℃,168 hr 100% strain, 100 ℃, 168 hr |
% | ASTM D573 | |
300% 应变,100℃,168 hr 300% strain, 100 ℃, 168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,100℃,336 hr 100% strain, 100 ℃, 336 hr |
% | ASTM D573 | |
300% 应变,100℃,336 hr 300% strain, 100 ℃, 336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,100℃,504 hr 100% strain, 100 ℃, 504 hr |
% | ASTM D573 | |
300% 应变,100℃,504 hr 300% strain, 100 ℃, 504 hr |
% | ASTM D573 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,125℃,70 hr 100% strain, 125 ℃, 70 hr |
% | ASTM D573 | |
300% 应变,125℃,70 hr 300% strain, 125 ℃, 70 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,125℃,168 hr 100% strain, 125 ℃, 168 hr |
% | ASTM D573 | |
300% 应变,125℃,168 hr 300% strain, 125 ℃, 168 hr |
% | ASTM D573 | |
125℃,336 hr 125℃,336 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,125℃,336 hr 100% strain, 125 ℃, 336 hr |
% | ASTM D573 | |
300% 应变,125℃,336 hr 300% strain, 125 ℃, 336 hr |
% | ASTM D573 | |
125℃,504 hr 125℃,504 hr |
% | ASTM D573 , ISO 216 | |
100% 应变,125℃,504 hr 100% strain, 125 ℃, 504 hr |
% | ASTM D573 | |
300% 应变,125℃,504 hr 300% strain, 125 ℃, 504 hr |
% | ASTM D573 | |
100% 应变 100℃,70 hr 100% strain at 100 ℃, 70 hr |
% | ISO 216 | |
300% 应变 100℃,70 hr 300% strain at 100 ℃, 70 hr |
% | ISO 216 | |
100% 应变 100℃,168 hr 100% strain at 100 ℃, 168 hr |
% | ISO 216 | |
300% 应变 100℃,168 hr 300% strain at 100 ℃, 168 hr |
% | ISO 216 | |
100% 应变 100℃,336 hr 100% strain at 100 ℃, 336 hours |
% | ISO 216 | |
300% 应变 100℃,336 hr 300% strain at 100 ℃, 336 hours |
% | ISO 216 | |
100% 应变 100℃,504 hr 100% strain at 100 ℃, 504 hr |
% | ISO 216 | |
300% 应变 100℃,504 hr 300% strain at 100 ℃, 504 hr |
% | ISO 216 | |
100% 应变 125℃,70 hr 100% strain 125 ℃, 70 hr |
% | ISO 216 | |
300% 应变 125℃,70 hr 300% strain 125 ℃, 70 hr |
% | ISO 216 | |
100% 应变 125℃,168 hr 100% strain 125 ℃, 168 hr |
% | ISO 216 | |
300% 应变 125℃,168 hr 300% strain 125 ℃, 168 hr |
% | ISO 216 | |
100% 应变 125℃,336 hr 100% strain 125 ℃, 336 hr |
% | ISO 216 | |
300% 应变 125℃,336 hr 300% strain 125 ℃, 336 hr |
% | ISO 216 | |
100% 应变 125℃,504 hr 100% strain 125 ℃, 504 hr |
% | ISO 216 | |
300% 应变 125℃,504 hr 300% strain 125 ℃, 504 hr |
% | ISO 216 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 , ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 , ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 , ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 , ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 , ISO 216 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D573 , ISO 216 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 , ISO 216 | |
125℃,336 hr 125℃,336 hr |
% | ASTM D573 , ISO 216 | |
125℃,504 hr 125℃,504 hr |
% | ASTM D573 , ISO 216 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 , ISO 216 | ||
支撐 D,100℃,70 hr Support D, 100 ℃, 70 hr |
ASTM D573 , ISO 216 | ||
支撐 D,100℃,168 hr Support D, 100 ℃, 168 hr |
ASTM D573 , ISO 216 | ||
支撐 D,100℃,336 hr Support D, 100 ℃, 336 hr |
ASTM D573 , ISO 216 | ||
支撐 D,100℃,504 hr Support D, 100 ℃, 504 hr |
ASTM D573 , ISO 216 | ||
支撐 D,125℃,70 hr Support D, 125 ℃, 70 hr |
ASTM D573 , ISO 216 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr |
ASTM D573 , ISO 216 | ||
支撐 D,125℃,336 hr Support D, 125 ℃, 336 hr |
ASTM D573 , ISO 216 | ||
支撐 D,125℃,504 hr Support D, 125 ℃, 504 hr |
ASTM D573 , ISO 216 | ||
拉伸强度的变化率 The rate of change in tensile strength |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
100% 应变,23℃,70 hr,C级标准燃料 100% strain, 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
300% 应变,23℃,70 hr,C级标准燃料 300% strain, 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,70 hr,在基准燃料A中 23 ℃, 70 hr, in reference fuel A |
% | ASTM D471 | |
100% 应变,23℃,70 hr,在基准燃料A中 100% 应变, 23°C, 70 hr, 在基准燃料A中 |
% | ASTM D471 | |
300% 应变,23℃,70 hr,在基准燃料A中 300% strain, 23 ℃, 70 hr, in reference fuel A |
% | ASTM D471 | |
23℃,168 hr,C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
100% 应变,23℃,168 hr,C级标准燃料 100% strain, 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
300% 应变,23℃,168 hr,C级标准燃料 300% strain, 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,168 hr,在基准燃料A中 23 ℃, 168 hr, in reference fuel A |
% | ASTM D471 | |
100% 应变,23℃,168 hr,在基准燃料A中 100% strain, 23 ℃, 168 hr, in reference fuel A |
% | ASTM D471 | |
300% 应变,23℃,168 hr,在基准燃料A中 300% strain, 23 ℃, 168 hr, in reference fuel A |
% | ASTM D471 | |
23℃,336 hr,C级标准燃料 23 ℃, 336 hr, C-grade standard fuel |
% | ASTM D471 | |
100% 应变,23℃,336 hr,C级标准燃料 100% strain, 23 ℃, 336 hr, C-grade standard fuel |
% | ASTM D471 | |
300% 应变,23℃,336 hr,C级标准燃料 300% strain, 23 ℃, 336 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,336 hr,在基准燃料A中 23 ℃, 336 hr, in reference fuel A |
% | ASTM D471 | |
100% 应变,23℃,336 hr,在基准燃料A中 100% strain, 23 ℃, 336 hr, in reference fuel A |
% | ASTM D471 | |
300% 应变,23℃,336 hr,在基准燃料A中 300% strain, 23 ℃, 336 hr, in reference fuel A |
% | ASTM D471 | |
23℃,504 hr,C级标准燃料 23 ℃, 504 hr, C-grade standard fuel |
% | ASTM D471 | |
100% 应变,23℃,504 hr,C级标准燃料 100% strain, 23 ℃, 504 hr, C-grade standard fuel |
% | ASTM D471 | |
300% 应变,23℃,504 hr,C级标准燃料 300% strain, 23 ℃, 504 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,504 hr,在基准燃料A中 23 ℃, 504 hr, in reference fuel A |
% | ASTM D471 | |
100% 应变,23℃,504 hr,在基准燃料A中 100% strain, 23 ℃, 504 hr, in reference fuel A |
% | ASTM D471 | |
300% 应变,23℃,504 hr,在基准燃料A中 300% strain, 23 ℃, 504 hr, in reference fuel A |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100% 应变,100℃,70 hr,在ASTM #1油中 100% 应变, 100°C, 70 hr, 在ASTM #1油中 |
% | ASTM D471 , ISO 175 | |
300% 应变,100℃,70 hr,在ASTM #1油中 300% strain, 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% 应变,100℃,70 hr,在ASTM #3油中 100% strain, 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
300% 应变,100℃,70 hr,在ASTM #3油中 300% strain, 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,在ASTM #1油中 100 ℃, 168 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100% 应变,100℃,168 hr,在ASTM #1油中 100% strain, 100 ℃, 168 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
300% 应变,100℃,168 hr,在ASTM #1油中 300% strain, 100 ℃, 168 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,168 hr,在ASTM #3油中 100 ℃, 168 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% 应变,100℃,168 hr,在ASTM #3油中 100% strain, 100 ℃, 168 hr, in ASTM # 3 oil |
% | ASTM D471 | |
300% 应变,100℃,168 hr,在ASTM #3油中 300% strain, 100 ℃, 168 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,336 hr,在ASTM #1油中 100 ℃, 336 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100% 应变,100℃,336 hr,在ASTM #1油中 100% strain, 100 ℃, 336 hours, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
300% 应变,100℃,336 hr,在ASTM #1油中 300% strain, 100 ℃, 336 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,336 hr,在ASTM #3油中 100 ℃, 336 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% 应变,100℃,336 hr,在ASTM #3油中 100% strain, 100 ℃, 336 hours, in ASTM # 3 oil |
% | ASTM D471 | |
300% 应变,100℃,336 hr,在ASTM #3油中 300% strain, 100 ℃, 336 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,504 hr,在ASTM #1油中 100 ℃, 504 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100% 应变,100℃,504 hr,在ASTM #1油中 100% strain, 100 ℃, 504 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
300% 应变,100℃,504 hr,在ASTM #1油中 300% strain, 100 ℃, 504 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,504 hr,在ASTM #3油中 100 ℃, 504 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% 应变,100℃,504 hr,在ASTM #3油中 100% strain, 100 ℃, 504 hr, in ASTM # 3 oil |
% | ASTM D471 | |
300% 应变,100℃,504 hr,在ASTM #3油中 300% strain, 100 ℃, 504 hr, in ASTM # 3 oil |
% | ASTM D471 | |
23℃,70 hr,in Reference Fuel C 23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
100% 应变,23℃,70 hr,in Reference Fuel C 100% strain, 23 ℃, 70 hr, in Reference Fuel C |
% | ISO 175 | |
300% 应变,23℃,70 hr,in Reference Fuel C 300% strain, 23 ℃, 70 hr, in Reference Fuel C |
% | ISO 175 | |
23℃,70 hr,在参考燃料 A中(异辛烷) 23 ℃, 70 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
100% 应变,23℃,70 hr,在参考燃料 A中(异辛烷) 100% strain, 23 ℃, 70 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
300% 应变,23℃,70 hr,在参考燃料 A中(异辛烷) 300% strain, 23 ℃, 70 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel C 23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
100% 应变,23℃,168 hr,in Reference Fuel C 100% strain, 23 ℃, 168 hr, in Reference Fuel C |
% | ISO 175 | |
300% 应变,23℃,168 hr,in Reference Fuel C 300% strain, 23 ℃, 168 hr, in Reference Fuel C |
% | ISO 175 | |
23℃,168 hr,在参考燃料 A中(异辛烷) 23 ℃, 168 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
100% 应变,23℃,168 hr,在参考燃料 A中(异辛烷) 100% strain, 23 ℃, 168 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
300% 应变,23℃,168 hr,在参考燃料 A中(异辛烷) 300% strain, 23 ℃, 168 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
100% 应变,23℃,336 hr,in Reference Fuel C 100% strain, 23 ℃, 336 hr, in Reference Fuel C |
% | ISO 175 | |
300% 应变,23℃,336 hr,in Reference Fuel C 300% strain, 23 ℃, 336 hr, in Reference Fuel C |
% | ISO 175 | |
23℃,336 hr,在参考燃料 A中(异辛烷) 23 ℃, 336 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
100% 应变,23℃,336 hr,在参考燃料 A中(异辛烷) 100% strain, 23 ℃, 336 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
300% 应变,23℃,336 hr,在参考燃料 A中(异辛烷) 300% strain, 23 ℃, 336 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100% 应变,23℃,504 hr,in Reference Fuel C 100% strain, 23 ℃, 504 hr, in Reference Fuel C |
% | ISO 175 | |
300% 应变,23℃,504 hr,in Reference Fuel C 300% strain, 23 ℃, 504 hr, in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,在参考燃料 A中(异辛烷) 23 ℃, 504 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
100% 应变,23℃,504 hr,在参考燃料 A中(异辛烷) 100% strain, 23 ℃, 504 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
300% 应变,23℃,504 hr,在参考燃料 A中(异辛烷) 300% strain, 23 ℃, 504 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
100℃,70 hr,在 ASTM #3 油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% 应变,100℃,70 hr,在 ASTM #3 油中 100% strain, 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
300% 应变,100℃,70 hr,在 ASTM #3 油中 300% strain, 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,在 ASTM #3 油中 100 ℃, 168 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% 应变,100℃,168 hr,在 ASTM #3 油中 100% strain, 100 ℃, 168 hr, in ASTM # 3 oil |
% | ISO 175 | |
300% 应变,100℃,168 hr,在 ASTM #3 油中 300% strain, 100 ℃, 168 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,336 hr,在 ASTM #3 油中 100 ℃, 336 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% 应变,100℃,336 hr,在 ASTM #3 油中 100% strain, 100 ℃, 336 hours, in ASTM # 3 oil |
% | ISO 175 | |
300% 应变,100℃,336 hr,在 ASTM #3 油中 300% strain, 100 ℃, 336 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,504 hr,在 ASTM #3 油中 100 ℃, 504 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% 应变,100℃,504 hr,在 ASTM #3 油中 100% strain, 100 ℃, 504 hr, in ASTM # 3 oil |
% | ISO 175 | |
300% 应变,100℃,504 hr,在 ASTM #3 油中 300% strain, 100 ℃, 504 hr, in ASTM # 3 oil |
% | ISO 175 | |
极限伸长率的变化率 Change rate of ultimate elongation |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,70 hr,在基准燃料A中 23 ℃, 70 hr, in reference fuel A |
% | ASTM D471 | |
23℃,168 hr,C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,168 hr,在基准燃料A中 23 ℃, 168 hr, in reference fuel A |
% | ASTM D471 | |
23℃,336 hr,C级标准燃料 23 ℃, 336 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,336 hr,在基准燃料A中 23 ℃, 336 hr, in reference fuel A |
% | ASTM D471 | |
23℃,504 hr,C级标准燃料 23 ℃, 504 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,504 hr,在基准燃料A中 23 ℃, 504 hr, in reference fuel A |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,在ASTM #1油中 100 ℃, 168 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,168 hr,在ASTM #3油中 100 ℃, 168 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,336 hr,在ASTM #1油中 100 ℃, 336 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,336 hr,在ASTM #3油中 100 ℃, 336 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,504 hr,在ASTM #1油中 100 ℃, 504 hr, in ASTM # 1 oil |
% | ASTM D471 , ISO 175 | |
100℃,504 hr,在ASTM #3油中 100 ℃, 504 hr, in ASTM # 3 oil |
% | ASTM D471 | |
23℃,70 hr,in Reference Fuel C 23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,70 hr,在参考燃料 A中(异辛烷) 23 ℃, 70 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel C 23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,168 hr,在参考燃料 A中(异辛烷) 23 ℃, 168 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,336 hr,在参考燃料 A中(异辛烷) 23 ℃, 336 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,在参考燃料 A中(异辛烷) 23 ℃, 504 hr, in reference fuel A (isooctane) |
% | ISO 175 | |
100℃,70 hr,在 ASTM #3 油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,在 ASTM #3 油中 100 ℃, 168 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,336 hr,在 ASTM #3 油中 100 ℃, 336 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,504 hr,在 ASTM #3 油中 100 ℃, 504 hr, in ASTM # 3 oil |
% | ISO 175 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
|||
支撐 D,23℃,70 hr,在基准燃料C中 Support D, 23 ℃, 70 hr, in reference fuel C |
ASTM D471 , ISO 175 | ||
支撐 D,23℃,70 hr,在基准燃料A中 Support D, 23 ℃, 70 hr, in reference fuel A |
ASTM D471 | ||
支撐 D,23℃,168 hr,在基准燃料C中 Support D, 23 ℃, 168 hr, in reference fuel C |
ASTM D471 , ISO 175 | ||
支撐 D,23℃,168 hr,在基准燃料A中 Support D, 23 ℃, 168 hr, in reference fuel A |
ASTM D471 | ||
支撐 D,23℃,336 hr,在基准燃料C中 Support D, 23 ℃, 336 hr, in reference fuel C |
ASTM D471 , ISO 175 | ||
支撐 D,23℃,336 hr,在基准燃料A中 Support D, 23 ℃, 336 hr, in reference fuel A |
ASTM D471 | ||
支撐 D,23℃,504 hr,在基准燃料C中 Support D, 23 ℃, 504 hr, in reference fuel C |
ASTM D471 , ISO 175 | ||
支撐 D,23℃,504 hr,在基准燃料A中 Support D, 23 ℃, 504 hr, in reference fuel A |
ASTM D471 | ||
支撐 D,100℃,70 hr,在ASTM #1油中 Support D, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 , ISO 175 | ||
支撐 D,100℃,70 hr,在ASTM #3油中 Support D, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
支撐 D,100℃,168 hr,在ASTM #1油中 Support D, 100 ℃, 168 hr, in ASTM # 1 oil |
ASTM D471 , ISO 175 | ||
支撐 D,100℃,168 hr,在ASTM #3油中 Support D, 100 ℃, 168 hr, in ASTM # 3 oil |
ASTM D471 | ||
支撐 D,100℃,336 hr,在ASTM #1油中 Support D, 100 ℃, 336 hr, in ASTM # 1 oil |
ASTM D471 , ISO 175 | ||
支撐 D,100℃,336 hr,在ASTM #3油中 Support D, 100 ℃, 336 hr, in ASTM # 3 oil |
ASTM D471 | ||
支撐 D,100℃,504 hr,在ASTM #1油中 Support D, 100 ℃, 504 hr, in ASTM # 1 oil |
ASTM D471 , ISO 175 | ||
支撐 D,100℃,504 hr,在ASTM #3油中 Support D, 100 ℃, 504 hr, in ASTM # 3 oil |
ASTM D471 | ||
支撐 D,23℃,70 hr,在基准燃料A(异辛烷)中 支撐 D, 23°C, 70 hr, 在基准燃料 A 中(异辛烷 ) |
ISO 175 | ||
支撐 D,23℃,168 hr,在基准燃料A(异辛烷)中 Support D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ISO 175 | ||
支撐 D Support D |
|||
23℃,504 hr,在基准燃料 A 中,异辛烷 23 ℃, 504 hr, in reference fuel A, isooctane |
ISO 175 | ||
23℃,336 hr,在基准燃料 A 中,异辛烷 23 ℃, 336 hr, in reference fuel A, isooctane |
ISO 175 | ||
100℃,70 hr,在 ASTM #3 油中 100 ℃, 70 hr, in ASTM # 3 oil |
ISO 175 | ||
100℃,504 hr,在 ASTM #3 油中 100 ℃, 504 hr, in ASTM # 3 oil |
ISO 175 | ||
100℃,336 hr,在 ASTM #3 油中 100 ℃, 336 hr, in ASTM # 3 oil |
ISO 175 | ||
100℃,168 hr,在 ASTM #3 油中 100 ℃, 168 hr, in ASTM # 3 oil |
ISO 175 | ||
体积变化 Volume change |
|||
23℃,70 hr,A级标准燃料 23 ℃, 70 hr, A-grade standard fuel |
% | ASTM D471 | |
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,168 hr,A级标准燃料 23 ℃, 168 hr, A-grade standard fuel |
% | ASTM D471 | |
23℃,168 hr,C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,336 hr,A级标准燃料 23 ℃, 336 hr, A-grade standard fuel |
% | ASTM D471 | |
23℃,336 hr,C级标准燃料 23 ℃, 336 hr, C-grade standard fuel |
% | ASTM D471 | |
23℃,504 hr,A级标准燃料 23 ℃, 504 hr, A-grade standard fuel |
% | ASTM D471 | |
23℃,504 hr,C级标准燃料 23 ℃, 504 hr, C-grade standard fuel |
% | ASTM D471 | |
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,70 hr,ASTM 标准油(3号) 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
100℃,168 hr,ASTM 标准油(1号) 100 ℃, 168 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,168 hr,ASTM 标准油(3号) 100 ℃, 168 hr, ASTM standard oil (No. 3) |
% | ASTM D471 | |
100℃,336 hr,ASTM 标准油(1号) 100 ℃, 336 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,336 hr,ASTM 标准油(3号) 100 ℃, 336 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
100℃,504 hr,ASTM 标准油(1号) 100 ℃, 504 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,504 hr,ASTM 标准油(3号) 100 ℃, 504 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
23℃,70 hr,在基准燃料 A 中 23 ℃, 70 hr, in reference fuel A |
% | ISO 175 | |
23℃,70 hr,在基准燃料 C 中 23 ℃, 70 hr, in reference fuel C |
% | ISO 175 | |
23℃,168 hr,在基准燃料 A 中 23 ℃, 168 hr, in reference fuel A |
% | ISO 175 | |
23℃,168 hr,在基准燃料 C 中 23 ℃, 168 hr, in reference fuel C |
% | ISO 175 | |
23℃,336 hr,在基准燃料 A 中 23 ℃, 336 hr, in reference fuel A |
% | ISO 175 | |
23℃,336 hr,在基准燃料 C 中 23 ℃, 336 hr, in reference fuel C |
% | ISO 175 | |
23℃,504 hr,在基准燃料 A 中 23 ℃, 504 hr, in reference fuel A |
% | ISO 175 | |
23℃,504 hr,在基准燃料 C 中 23 ℃, 504 hr, in reference fuel C |
% | ISO 175 | |
100℃,70 hr,在 ASTM #3 油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,168 hr,在 ASTM #3 油中 100 ℃, 168 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,在ASTM #1油中 100 ℃, 168 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,336 hr,在 ASTM #3 油中 100 ℃, 336 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,336 hr,在ASTM #1油中 100 ℃, 336 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,504 hr,在 ASTM #3 油中 100 ℃, 504 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,504 hr,在ASTM #1油中 100 ℃, 504 hr, in ASTM # 1 oil |
% | ISO 175 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746,ISO 974 | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/50 , ASTM D1525 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩载荷 Compression load |
ASTM D575 | ||
10% 挠曲 10% deflection |
MPa | ASTM D575 | |
15% 挠曲 15% deflection |
MPa | ASTM D575 | |
2% 挠曲 2% deflection |
MPa | ASTM D575 | |
20% 挠曲 20% deflection |
MPa | ASTM D575 | |
25% 挠曲 25% deflection |
MPa | ASTM D575 | |
5% 挠曲 5% deflection |
MPa | ASTM D575 | |
50% 挠曲 50% deflection |
MPa | ASTM D575 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 , ISO 868 | ||
弯曲模量 Bending modulus |
ASTM D790 , ISO 178 | ||
23℃ 23℃ |
MPa | ASTM D790 , ISO 178 | |
70℃ 70℃ |
MPa | ASTM D790 , ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
北京:使用不可降解塑料袋最高罚10万
2021-05-02 搜料网资讯: 北京市发改委近日披露,今年北京市将开展塑料污染治理各领域的专项执法。据介绍,经营主体使用不可 降解塑料 购物袋,将按有关规定依法处以一万元以上十万元以下 |
北京:使用不可降解塑料袋最高罚10万 搜料网资讯:北京市发改委近日披露,今年北京市将开展塑料污染治理各领域的专项执法。据介绍,经营主体使用不可降解塑料购物袋,将按有关规定依法处以一万元以上十万元以下的罚款。根据今年限塑的工作要点,北京市将加大对违规生产和销售厚度小于0.025毫米的超薄塑料购物袋、厚度小于0.01毫米的聚乙烯地膜、一次性发泡塑料餐具、一次性塑料棉签等执法力度。
随着2020年发布《关于进一步加强塑料污染治理的意见》,我国正式加入“禁塑”行列、步入可降解时代。目前我国废弃塑料总量高,年均在4200万吨,其中,塑料袋折合塑料消费超过400万吨,农用地膜折合塑料的消费量也超百万吨。来自中国塑协塑料再生利用专业委员会的数据显示,全国每天使用塑料袋约30亿个。截至2019年,塑料袋年使用量超过400万吨。巨大的消耗量以及对环境造成的负面影响,使社会各界对塑料污染治理普遍关注。 从2020年11月10日,市发改委等部门开始对《北京市塑料污染治理行动计划(2020—2025年)(征求意见稿)》征求意见。根据征求意见稿,北京“限塑10条”禁止、限制部分塑料制品的生产、销售,聚焦六大行业强化减塑力度。 2020年北京“限塑令”规定 <禁止生产销售超薄塑料购物袋> 严格落实国家有关要求,全市范围内禁止生产和销售厚度小于0.025毫米的超薄塑料购物袋、厚度小于0.01毫米的聚乙烯农用地膜; 到2020年底,禁止生产和销售一次性发泡塑料餐具、一次性塑料棉签,禁止生产含塑料微珠的日化产品; 到2022年底,禁止销售含塑料微珠的日化产品。市级有关部门要加大监督执法力度,确保禁限措施有效实施。 <六大重点行业开展塑料污染治理> (1)餐饮业:年底将禁用不可降解一次性塑料吸管 到2020年底,全市餐饮行业禁止使用不可降解一次性塑料吸管、咖啡搅拌棒;本市建成区外卖(含堂食打包)服务禁止使用不可降解塑料袋;本市建成区、景区景点堂食服务禁止使用不可降解一次性塑料餐具。鼓励餐饮堂食服务采用可清洗消毒、重复使用的餐具。 (2)外卖:发放“绿色优惠券”引导消费者 2021年底前,本市鼓励外卖平台在点单环节设置“无需餐具”等选项,并给予积分等形式的奖励。鼓励外卖平台加大宣传力度,树立主动使用可降解餐盒、可重复利用餐盒(具)餐饮企业履行生态环保责任的良好形象,并通过发放平台“专属绿色优惠券”等措施引导消费者选择。 (3)批发零售:年底将禁用不可降解塑料袋 到2020年底,本市建成区的商场、超市、药店、书店等零售业门店(含配送服务)禁止使用不可降解塑料袋。 到2023年底,集贸市场塑料购物袋全面实现集中购销,鼓励城市副中心、生态涵养区率先在镇乡和农村集市停止使用不可降解塑料袋。到2025年底,本市建成区集贸市场禁止使用不可降解塑料袋。 本市鼓励探索逐步实施对塑料连卷袋明码标价并在商品价外单独收取塑料连卷袋价款,引导消费者减少塑料连卷袋使用量。 (4)电商快递:2025年底将禁用不可降解塑料胶带 到2020年底,全市邮政快递及电商配送网点“瘦身胶带”封装比例达到90%、循环中转袋使用率达到95%以上。 到2022年底,全市邮政快递网点禁止使用不可降解塑料包装袋、编织袋等,循环中转袋使用率达到100%。 到2025年底,全市邮政快递网点禁止使用不可降解塑料胶带。 (5)住宿会展:不得主动提供六类一次性用品 全市宾馆按照《北京市宾馆不得主动提供的一次性用品目录》要求,不得主动提供六类一次性用品,可通过设置自助购买机、提供续充型洗洁剂等方式提供相关服务。到2025年底,根据实施情况逐步扩大目录范围,并将实施范围扩大至民宿。 (6)农业生产:推广使用0.014毫米(含)以上地膜 根据《关于加快推进农用地膜污染防治的意见》《农用薄膜管理办法》要求,在全市农村地区推广使用0.014毫米(含)以上地膜,开展全生物降解地膜试验示范和农膜残留检测,采取以旧换新、经营主体上交、专业组织回收等方式,推进废旧农膜和农药、肥料包装废弃物回收处置工作,妥善处理废弃育苗盘和节水灌溉材料等农业塑料废弃物。 到2022年底,基本建立政府支持、市场主导的废旧农膜和农药、肥料包装废弃物回收处置体系,农膜回收率达到90%以上。 据悉,北京市加快推动建立“1+1+N”的塑料污染治理政策体系:《生活垃圾管理条例》法规保障作用日益凸显;《行动计划》的统筹作用初步形成;“N”项专项工作方案、标准不断补充完善,目前专项工作方案已出台10项。部分区结合本地实际,制定了区级塑料污染治理行动计划。例如,延庆区以城乡环境整治为契机,将塑料污染治理纳入文明旅游诚信经营专项行动。平谷区成立区级塑料污染治理行动计划工作专班,计划率先实现在镇乡和农村集市停止使用不可降解塑料袋。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |