牌号简介 About |
---|
产品说明TOPAS® 5013F-04是一种高温薄膜挤出级的混合物。它是一种高透明非晶树脂,具有高流动性、高硬度、防潮性、耐化学性、热成型性和纯度,适用于食品和医疗保健应用。它被用于单层铸造混合物,以及铸造和吹塑过程中的共挤混合物中,用于各种薄膜和片材产品,在耐热泡罩、热填充和易撕裂包装等应用中需要优良的光学性能。如果不需要高温性能,我们还提供较低的玻璃化转变温度(TG)等级的TOPA。选定用途装饰膜和片材一般包装食品包装吹塑膜保健和食品接触主要属性光泽、硬度、耐化学性、易形成或线性撕裂、耐热性、热填充、不含双酚A、邻苯二甲酸盐或卤素的光泽、高强度和高生产率、广泛的法规遵从性包装和薄膜挤压用品级 Product Description TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS. Selected Applications Decorative film and sheet General packaging Food packaging Blown film Food contact Leading Attributes Gloss, hardness, chemical resistance, forming Easy or linear tear, heat resistance, hot fill, gloss Not manufactured with BPA, phthalates, or halogens High strength and high productivity Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 6013F-04 - high temperature grade with standard flow |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
< 0.10 | g/10min | ISO 1133 |
230℃,2.16kg 230℃,2.16kg |
8.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
< 0.100 | cm³/10min | ISO 1133 |
230℃,2.16 kg 230℃,2.16 kg |
9.00 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸模量 Tensile modulus |
ISO 527-3/1 | ||
MD,70 µm,铸造薄膜 MD, 70 µ m, cast thin film |
MPa | ISO 527-3/1 | |
TD,70 µm,铸造薄膜 TD, 70 µ m, cast thin film |
MPa | ISO 527-3/1 | |
拉伸强度 tensile strength |
ISO 527-3/50 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3/50 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3/50 | |
拉伸应变 Tensile strain |
ISO 527-3/50 | ||
MD,断裂,70 µm,铸造薄膜 MD, fracture, 70 µ m, cast thin film |
% | ISO 527-3/50 | |
TD,断裂,70 µm,铸造薄膜 TD, fracture, 70 µ m, cast thin film |
% | ISO 527-3/50 | |
落锤冲击 Drop hammer impact |
|||
70 µm,铸造薄膜 70 µ m, cast thin film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:70 µm,铸造薄膜 MD: 70 µ m, cast thin film |
N | ISO 6383-2 | |
TD:70 µm,铸造薄膜 TD: 70 µ m, cast thin film |
N | ISO 6383-2 | |
透氧率 Oxygen permeability |
|||
23℃,70 µm,挤塑薄膜,50% RH 23 ℃, 70 µ m, extruded film, 50% RH |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
70 µm,38℃,铸造薄膜,90% RH 70 µ m, 38 ℃, cast thin film, 90% RH |
g·mm/m²/atm/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,70.0 µm,铸造薄膜 60 °, 70.0 µ m, cast thin film |
ISO 2813 | ||
雾度 Haze |
|||
70.0 µm,铸造薄膜 70.0 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |