| 牌号简介 About |
|---|
| HT5303是一种高密度聚乙烯，己烯共聚物，通过Unipol工艺生产，并开发用于制造波纹管。它在刚度、冲击和抗应力开裂以及高抗氧化降解性之间表现出适当的平衡。用途：用于能源、电信电缆保护及道路、运动场排水的波纹管。工艺：管材挤出。 HT5303 is a high density polyethylene, hexene copolymer, produced through Unipol® process and developed for the manufacturing of corrugated pipes. It exhibits an appropriate balance between stiffness, impact and stress cracking resistance, as well as a high resistance to oxidative degradation. Application: Corrugated pipes for energy and telecom cables protection and for drainage of roads and sports fields. Process: Pipe Extrusion. |
产品描述 Product Description
用途：波纹管;管道系统;
加工条件：管路挤出成型
性能特点： 机械强度好; 己烯共聚单体; 冲击性能好; 抗应力开裂; Good Rigidity,High impact resistance,Hexene copolymers,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.954 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.30 | g/10min | ASTM D1238 |
|
190℃，21.6kg 190℃，21.6kg |
26 | g/10min | ASTM D1238 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
ASTM D1693 | ||
|
50 ℃，2.00 mm，10%非离子表面活性剂，模压成型，F50 50 ℃, 2.00 mm, 10% non-ionic surfactant, molded, F50 |
43.0 | hr | ASTM D1693 |
|
50 ℃，2.00 mm，100%非离子表面活性剂，模压成型，F50 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 |
168 | hr | ASTM D1693 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
模压成型 Compression Molding |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火，模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
|
氧感应时间 Oxygen sensing time 3 |
|||
|
200℃ 200℃ 3 |
min | ASTM D3895 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
NCLS NCLS 3 |
hr | ASTM F2136 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，模压成型 Shaw's D, molded |
ASTM D2240 | ||
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
屈服，模压成型 Yield, molding |
MPa | ASTM D638 | |
|
断裂，模压成型 Fracture, molded |
MPa | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割，模压成型 1% cut, molded |
MPa | ASTM D790 | |
| 备注 |
|---|
| 2 压 力1 (10N) |
| 3 Compression Molded |
|
【新闻资讯】查看全部 
到2025年印度将占亚太地区LNG再气化产能21%
2021-11-14 搜料网资讯： 据油气新闻11月5日消息称，全球领先的数据和分析公司GlobalData表示，2021年至2025年间，印度预计将成为亚洲LNG再气化产能增加量第二高的国家，到2025年，将占该地区总新增 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付