HDPE，Braskem PE HT5303对比HDPE，Petrothene® LB560201物性表,价格行情_搜料

牌号信息	Braskem PE HT5303 物性表 HDPE & 巴西布拉斯科指导价格：暂无塑料库存：缺货	Petrothene® LB560201 物性表 HDPE & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货
牌号简介	HT5303是一种高密度聚乙烯，己烯共聚物，通过Unipol工艺生产，并开发用于制造波纹管。它在刚度、冲击和抗应力开裂以及高抗氧化降解性之间表现出适当的平衡。用途：用于能源、电信电缆保护及道路、运动场排水的波纹管。工艺：管材挤出。 HT5303 is a high density polyethylene, hexene copolymer, produced through Unipol® process and developed for the manufacturing of corrugated pipes. It exhibits an appropriate balance between stiffness, impact and stress cracking resistance, as well as a high resistance to oxidative degradation. Application: Corrugated pipes for energy and telecom cables protection and for drainage of roads and sports fields. Process: Pipe Extrusion.	该系列聚乙烯树脂具有优异的耐环境应力、抗裂性和刚度。典型的应用包括家用化学品瓶，如漂白剂、清洁剂和洗涤剂。 Petrothene LB560201 is a high density polyethylene resin that exhibits good stiffness and environmental stress crack resistance. Typical applications include bottles for household chemicals such as bleach, cleaners and detergents.

产品描述
厂家：	巴西布拉斯科 Braskem	荷兰利安德巴塞尔 LyondellBasell
类别：	HDPE HDPE	HDPE HDPE
填料：
用途：	波纹管,管道系统	瓶子
性能特点：	机械强度好,冲击性能好,己烯共聚单体,抗应力开裂 Good Rigidity,High impact resistance,Hexene copolymers,High ESCR	机械强度好,食品接触,抗应力开裂 Good Rigidity,Food contact compliance,High ESCR
加工条件：	管路挤出成型	吹塑成型

技术参数

物理性能
PHYSICAL Braskem PE HT5303 Petrothene® LB560201 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

密度
Density g/cm³ ASTM D792

抗环境应力开裂(50 ℃，10%润湿剂，F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

抗环境应力开裂(50 ℃，2.00 mm，10%非离子表面活性剂，模压成型，F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

抗环境应力开裂(50 ℃，2.00 mm，100%非离子表面活性剂，模压成型，F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(190℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Braskem PE HT5303 Petrothene® LB560201 单位
UNIT 测试方法
TEST METHOD

Tensile Impact
Tensile Impact J/cm ASTM D1822

悬臂梁缺口冲击强度(模压成型)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Braskem PE HT5303 Petrothene® LB560201 单位
UNIT 测试方法
TEST METHOD

氧感应时间(200℃)
Oxygen sensing time min ASTM D3895

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，模压成型)
Hot deformation temperature ℃ ASTM D648

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

脆化温度
Embrittlement temperature ℃ ASTM D746

补充信息
Braskem PE HT5303 Petrothene® LB560201 单位
UNIT 测试方法
TEST METHOD

NCLS
NCLS hr ASTM F2136

机械性能
MECHANICAL Braskem PE HT5303 Petrothene® LB560201 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(1% 正割，模压成型)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(屈服，模压成型)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂，模压成型)
tensile strength MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D，模压成型)
Shore hardness ASTM D2240

备注

2 压力1 (10N)

3 Compression Molded

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
补充信息
机械性能
加工方式
备注