| 牌号简介 About |
|---|
| 高密度聚乙烯用于制造大桶、漂白瓶、购物袋、板条箱、网和桶。强硬的。僵硬的重型的。具有很高的耐化学性。这些品质使聚乙烯适合于各种工业产品。吹塑薄膜：购物袋和杂货袋管道：压力和非压力管道吹塑：家用和工业化学品瓶，大桶注射成型：托盘、板条箱、箱子、托盘、玩具、家居用品、盖子 EVALENE ® HJ04601 has narrow molecular weight distribution and is specifically intended for use in injection molding applications requiring superior overall mechanical properties. It is designed to deliver an outstanding combination of long-term strength and durability. EVALENE ® HJ04601 is UV stabilized for excellent outdoor performance and weatherability resulting in wide end-use latitude. FEATURES Medium Flow Very high Izod impact strength High stiffness and rigidity High environmental stress crack resistance (ESCR) Meets Philippine FDA food contact requirements Halal-certified TYPICAL APPLICATIONS Pallets Dunnage trays Crates Industrial parts |
产品描述 Product Description
用途：容器;装货箱;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 耐化学性; 韧性好; 耐候抗UV; Good Rigidity,Weather resistance is good,Good flexibility,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 2 |
0.960 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
4.0 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD：48 hrs MD：48 hrs |
1.0 到 1.7 | % | 内部方法 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
10%非离子洗涤剂，F50 10% non-ionic detergent, F50 |
3.80 | hr | ASTM D1693B |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 6 |
|||
|
23℃ 23℃ 6 |
160 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
拉伸模量 Tensile modulus 3 |
|||
|
1% 正割 1% secant 3 |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength 4 |
|||
|
屈服 yield 4 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 4 |
|||
|
屈服 yield 4 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 5 |
|||
|
1% 正割 1% secant 5 |
MPa | ASTM D790-A | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.20 in/min |
| 3 2.0 in/min |
|
【新闻资讯】查看全部 
零部件日趋大型化推进模具大型化开展
2016-12-14 近年来，随着我国模具行业结构调整步伐加快，模具越来越趋向大型化、精密化、复杂化方向发展，这是由于高生产效率要求而决定的。为了提高生产效率而发展起来的“一模多腔”技术正在得到越来越广泛的应用。很显然，同样的一次注塑过程可以同时制造多个产品，生产效率自然翻番了。而另外一个原因则是零部件也日趋大型化了，也这直接导致了模具必须大型化。 面对模具和零件日趋大型化的发展，人们都困扰于如何满足大型模具和零件越来越高的表面精度要求?如何延长大型模具和零部件的使用寿命，而同时又要兼顾耐磨、防 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付