牌号简介 About |
---|
Noryl NH4030B树脂NH4030B是一种改进的PPE-HIPS混合物,具有良好的非卤化阻燃性平衡、燃烧时的低烟产生和轻重量部件的低比重。Noryl NH4030B可定制颜色,可能是需要轻量零件的应用的理想材料,可以通过注射成型或挤压技术进行加工。 NH4030B is a modified PPE-HIPS blend that presents an excellent balance of non halogenated flame retardance, lower smoke production upon burning and low specific gravity for light weight parts. NORYL NH4030B is available in custom colors and may be an excellent material candidate for applications requiring light weight parts and may be processed by injection molding or extrusion techniques. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PPO(PPE)+PS PPO(PPE)+PS
颜色:可用颜色
加工条件:片材挤出成型
性能特点: 无卤; 低烟; 阻燃; 低密度; Low smoke,Halogen free,Flame Characteristics,Low density
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.11 | g/cm³ | ASTM D792 |
密度 Density |
1.11 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
280℃,5.0kg 280℃,5.0kg |
18 | g/10min | ASTM D1238 |
300℃,5.0kg 300℃,5.0kg |
43 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
280℃,5 kg 280℃,5 kg |
17.6 | cm³/10min | ISO 1133 |
300℃,5 kg 300℃,5 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Draeger Tube Toxicity Draeger Tube Toxicity 11 |
|||
Flaming:1.52 mm Flaming:1.52 mm |
|||
Non-Flaming:1.52 mm Non-Flaming:1.52 mm |
|||
Flame Spread Index(1.52 mm) Flame Spread Index(1.52 mm) |
ASTM E162 | ||
NBS烟雾密度 NBS smoke density |
ASTM E662 | ||
Flaming,20 min:3.20 mm Flaming,20 min:3.20 mm |
ASTM E662 | ||
Flaming,4 min:1.52 mm Flaming,4 min:1.52 mm |
ASTM E662 | ||
Flaming,4 min:3.20 mm Flaming,4 min:3.20 mm |
ASTM E662 | ||
Non-Flaming,4 min:1.52 mm Non-Flaming,4 min:1.52 mm |
ASTM E662 | ||
垂直燃烧测试 Vertical combustion test |
FAR 25.853 | ||
Test a(60 s,1.52 mm),passes at Test a(60 s,1.52 mm),passes at |
hr | FAR 25.853 | |
Test b(12 s,1.52 mm),passes at Test b(12 s,1.52 mm),passes at |
sec | FAR 25.853 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
11 Tested according to AITM 3.0005, ABD0031 |
【新闻资讯】查看全部
以色列计划至2030年只使用可再生能源及天然气
2020-11-21 搜料网资讯: 据阿纳多卢新闻11月9日消息称,在以色列外交部组织的一次虚拟会议上,以色列能源部部长埃胡德阿迪里表示,以色列计划在2030年前满足天然气和可再生能源的所有能源需 |
以色列计划至2030年只使用可再生能源及天然气 搜料网资讯:阿迪里说,他的国家正计划增加可再生能源的产能,特别是太阳能光伏发电。 阿迪里说:“到2030年,我们将达到30%的可再生能源和70%的天然气。我们想要尽可能多的可再生能源。到2030年,我们计划开发16吉瓦(GW)的可再生能源,特别是太阳能。” 以色列目前所有燃料来源的总装机容量为16吉瓦,但阿迪里表示,该国将通过发行新的可再生能源招标书,将这一容量提高一倍,同时在2025年之前逐步淘汰煤炭。 他说:“2025年后我们将不再使用煤炭,我们将在10年内减少90%的污染物。” 截至2019年底,煤炭发电在该国能源结构中的份额为30%,可再生能源的份额为5%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求
- 阅读全文
NORYL树脂光伏接线盒
1-NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度;
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
收起
抱歉!暂无数据。