PPO(PPE)+PS，NORYL™ NH4030B resin对比PPO(PPE)+PS，NORYL™ PKN4775F resin物性表,价格行情_搜料

牌号信息	NORYL™ NH4030B resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：60900.0元/吨塑料库存： 10000kg	NORYL™ PKN4775F resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Noryl NH4030B树脂NH4030B是一种改进的PPE-HIPS混合物，具有良好的非卤化阻燃性平衡、燃烧时的低烟产生和轻重量部件的低比重。Noryl NH4030B可定制颜色，可能是需要轻量零件的应用的理想材料，可以通过注射成型或挤压技术进行加工。 NH4030B is a modified PPE-HIPS blend that presents an excellent balance of non halogenated flame retardance, lower smoke production upon burning and low specific gravity for light weight parts. NORYL NH4030B is available in custom colors and may be an excellent material candidate for applications requiring light weight parts and may be processed by injection molding or extrusion techniques.	PPE + PS共混物。不透明的符合FDA规定，颜色有限。高温。高温下的模量。ESCR性能好。薄壁挤压和注射成型。典型应用包括高性能应用程序的打包。 PPE+PS blend. Opaque. FDA compliant in limited colors. High heat. Modulus at elevated temperature. Good ESCR performance. Thin wall extrusion and injection molding. Typical applications include packaging for high performance applications.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS PPO(PPE)+PS	PPO(PPE)+PS PPO(PPE)+PS
填料：
用途：		包装
性能特点：	低烟,无卤,阻燃,低密度 Low smoke,Halogen free,Flame Characteristics,Low density	耐高温,抗应力开裂 High Heat Resistance,High ESCR
加工条件：	片材挤出成型	片材挤出成型

技术参数

物理性能
PHYSICAL NORYL™ NH4030B resin NORYL™ PKN4775F resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(300℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL NORYL™ NH4030B resin NORYL™ PKN4775F resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT NORYL™ NH4030B resin NORYL™ PKN4775F resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL NORYL™ NH4030B resin NORYL™ PKN4775F resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY NORYL™ NH4030B resin NORYL™ PKN4775F resin 单位
UNIT 测试方法
TEST METHOD

Draeger Tube Toxicity(Flaming：1.52 mm)
Draeger Tube Toxicity

Draeger Tube Toxicity(Non-Flaming：1.52 mm)
Draeger Tube Toxicity

Flame Spread Index(1.52 mm)
Flame Spread Index（1.52 mm） ASTM E162

NBS烟雾密度(Flaming，20 min：3.20 mm)
NBS smoke density ASTM E662

NBS烟雾密度(Flaming，4 min：1.52 mm)
NBS smoke density ASTM E662

NBS烟雾密度(Flaming，4 min：3.20 mm)
NBS smoke density ASTM E662

NBS烟雾密度(Non-Flaming，4 min：1.52 mm)
NBS smoke density ASTM E662

垂直燃烧测试(Test a(60 s，1.52 mm)，passes at)
Vertical combustion test hr FAR 25.853

垂直燃烧测试(Test b(12 s，1.52 mm)，passes at)
Vertical combustion test sec FAR 25.853

加工方式

挤出 NORYL™ NH4030B resin NORYL™ PKN4775F resin 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

接头温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)

11 Tested according to AITM 3.0005, ABD0031