牌号简介 About |
---|
HD 6908是一种均聚物,具有卓越的挺度,并在加工性和低温抗冲击性之间具有良好的平衡。 该树脂可理想地用于要求极高挺度或可以减薄的物品。 该材料在结构泡沫物品中具有卓越的性能。 HD 6908 is a homopolymer with outstanding stiffness with a good balance of processability and cold temperature impact performance. This resin is ideally suited for articles requiring very high stiffness or enable down-gauging. This material offers excellent performance in structural foam articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
8.2 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,F50 10% non-ionic detergent, F50 |
3.33 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
30.0 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
ASTM D790B | ||
1% 正割 1% secant |
1890 | MPa | ASTM D790-B |
2% 正割 2% secant |
1600 | MPa | ASTM D790-B |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃ -40℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648-B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
华塑股份再曝伤亡事故 上市或遥遥无期
2021-05-18 搜料网资讯: 对于化工企业而言,生产安全和环保是重中之重,而安徽华塑股份有限公司(以下简称华塑股份)在这两方面却屡屡被罚饱受诟病,尤其在IPO期间,其募投项目竟发生安全事 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |