牌号简介 About |
---|
Radel® R-7700聚苯砜片材是专为飞机内部应用而开发的。通过使用专有的阻燃包装,该树脂具有低放热、低发烟和低毒气体排放,从而符合联邦航空管理局法规14CFR第25.853部分附录F的要求。此外,它具有优异的抗冲击性,满足航空航天流体,甚至是不受腐蚀的典型工业要求。R应力。Radel® R-7700以颗粒和薄片形式提供。Radel® R-7700板可以形成大型复杂的几何形状,相对容易在传统的热成型设备。更多信息,请参考技术公告热成型Radel® R-7700表。提供多种自定义颜色 Radel® R-7700 polyphenylsulfone sheet was developed specifically for aircraft interior applications. Through the use of a proprietary flame retardant package, this resin offers low heat release, low smoke generation and low toxic gas emissions, thereby complying with the FAA regulation 14CFR Part 25.853 Appendix F. In addition, it has excellent impact resistance and meets typical industry requirements for resistance to aerospace fluids, even under stress. Radel® R-7700 is available in pellets and sheet form. Radel® R-7700 sheet can be formed into large complex geometries with relative ease on conventional thermoforming equipment. Please reference the Technical Bulletin Thermoforming Radel® R-7700 Sheet for additional information. Available in several custom colors |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 到 1.42 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.35 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
3.18 mm 3.18 mm |
2280 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
3.18 mm 3.18 mm |
58.6 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
15 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
3.18 mm 3.18 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.18 mm 3.18 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
ASTM D256 | ||
落锤冲击 Drop hammer impact |
|||
3.2 mm 3.2 mm |
J | BS 7271 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
毒气排放 Toxic gas emissions |
|||
氮气体,4分钟时 Nitrogen gas, at 4 minutes 2 |
ppm | ||
氟化氢 Hydrogen fluoride 3 |
ppm | ||
硫氧化物,4分钟时 Sulfur oxides, at 4 minutes 4 |
ppm | ||
氯化氢 Hydrogen chloride 5 |
ppm | ||
氰化氢,4分钟时 Hydrogen cyanide, at 4 minutes 6 |
ppm | ||
一氧化碳,4分钟时 Carbon monoxide at 4 minutes 7 |
ppm | ||
放热 exothermic |
Ohio State University | ||
2 分钟:1.52 到 3.18 mm 2 minutes: 1.52 to 3.18 mm 8 |
kW·min/m² | Ohio State University | |
峰值速率:1.52 到 3.18 mm Peak rate: 1.52 to 3.18 mm 9 |
kW/m² | Ohio State University | |
烟雾密度 Smoke density |
ASTM F814 | ||
比光密度,1.5 分钟时 Specific optical density at 1.5 minutes 10 |
Ds | ASTM F814 | |
最大比光密度,4分钟时 Maximum specific optical density at 4 minutes 11 |
Ds | ASTM F814 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 燃烧方式;BMS规格限制 = 60 ppm; ATS 1000.001 规格限制= 100 ppm |
3 燃烧方式; BMS规格限制 = 60 ppm;ATS 1000.001 规格限制= 50 ppm |
4 燃烧方式: BMS规格限制 = 30 ppm; ATS 1000.001 规格限制= 100 ppm |
5 燃烧方式; BMS规格限制 = 60 ppm; ATS 1000.001 规格限制 = 500 ppm |
6 燃烧方式; BMS规格限制 = 60 ppm; ATS 1000.001规格限制 = 150 ppm |
7 燃烧方式: BMS 规格限制 = 500 ppm;ATS 1000.001 规格限制= 3500 ppm |
8 美国联邦航空局的要求,14CFR PART 25.853 附录 F: 65 KW-min/m² |
9 美国联邦航空局的要求, 14CFR PART 25.853 附录 F: 65 KW/m² |
10 燃烧方式 |
11 燃烧方式; FAA行业要求: 200 |
【新闻资讯】查看全部
大家电出口海外成绩亮眼
2021-06-25 搜料网资讯: 海关总署数据显示,今年1-3月,中国家用电器出口总额为1479.4亿元,同比增长63.4%。中国家电出海正迎来新的高速增长期,进一步巩固着世界家电生产中心地位。传统家电 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |