Bayflex XGT-16黑色是一种用于反应注射成型(RIM)工艺的黑色弹性聚氨酯系统。配制的体系分为两种液体组分:A组分为二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚多元醇体系。注:多元醇组分相在静置时分离,使用前必须通过机械方式彻底混合。Bayflex XGT-16黑色系统在室温下的弯曲模量为16000 psi*。它用于需要优良冲击性能的应用中,如公共汽车和其他车辆的缓冲器。与任何产品一样,在给定应用中使用Bayflex XGT-16黑色系统必须由用户提前进行测试(包括但不限于现场测试),以确定其适用性。 Bayflex XGT-16 Black is a black-pigmented elastomeric polyurethane system used in the reaction injection molding (RIM) process. The formulated system is supplied as two liquid components: Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. Note: The polyol component phase-separates upon standing and must be thoroughly mixed via mechanical means prior to use. Bayflex XGT-16 Black system has a flexural modulus of 16,000 psi* at room temperature. It is used in applications requiring excellent impact properties, such as bumpers for buses and other vehicles. As with any product, use of the Bayflex XGT-16 Black system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 , ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.80 到 0.90 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
16.5 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
250 | % | ASTM D412 |
撕裂强度 tear strength 2 |
|||
3.18 mm 3.18 mm 2 |
78.8 | kN/m | ASTM D624 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,3.18 mm Shaw A, 3.18 mm |
ASTM D2240 | ||
邵氏 D,3.18 mm Shaw D, 3.18 mm |
ASTM D2240 | ||
弯曲模量 Bending modulus |
|||
3.18 mm 3.18 mm |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1.0E+6 g,H-18 转轮 1000 cycles, 1.0E+6 g, H-18 wheels |
mg | ASTM D1044 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 3 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
30℃ 30℃ |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 1.05 Index |
【新闻资讯】查看全部
我国持续对韩泰两国出口PTA征收反倾销税
2016-08-11 8月10日,商务部发布公告,自2016年8月11日起,对原产于韩国和泰国的进口精对苯二甲酸(PTA)继续征收反倾销税,实施期限5年。 2010年8月12日,商务部决定对原产于韩国和泰国的进口PTA最终反倾销措施,反倾销税征收范围为2%~20.1%,实施期限为自2010年8月12日起5年。 2015年8月10日,应国内PTA产业申请,该案所适用的反倾销措施进行期终复审调查。本次复审的倾销调查期为2014年4月1日至2015年3月31日,产业损害调查期为2011 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |