牌号简介 About |
---|
ADIPRENE L 42是一种液态聚氨酯弹性体,当用MBCA固化时,可产生硬度为80硬度的优质硫化胶。ADIPRENE L 42产品具有良好的撕裂强度、耐磨性和良好的弹性寿命。它们在-80°F(-62°C)和-130°F(-90°C)的脆性温度下具有10000 psi(703 kg/sq.cm.)的扭转模量,在低温下非常灵活。已发现,Adiprene L 42适用于制备辊、实心轮胎、隔膜、靴,以及其他需要良好弹性寿命的应用。还应考虑制作密封件、衬套和安装件,以便在极低温度下使用。ADIPRENE L 42的加工和处理特点与ADIPRENE L-100相似,可以在与处理ADIPRENE L-100相同类型的自动混合设备中进行加工。 ADIPRENE L 42 is a liquid urethane elastomer which yields high quality vulcanizates of 80 durometer A hardness when cured with MBCA. ADIPRENE L 42 products have good tear strength, good abrasion resistance, and excellent flex life. They are very flexible at low temperatures having a torsional modulus of 10,000 psi (703 kg./sq. cm.) at -80°F (-62°C), and a brittleness temperature of -130°F (-90°C). ADIPRENE L 42 has been found suitable for the preparation of rolls, solid tires, diaphragms, boots, and for other applications where good flex life is needed. It should also be considered for making seals, bushings, and mountings for use at very low temperatures. ADIPRENE L 42 resembles ADIPRENE L-100 in its processing and handling characteristics, and can be processed in the same type of automatic mixing equipment used to process ADIPRENE L-100. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.07 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,100℃ Shore A, 100 ℃ |
80 | ASTM D2240 | |
邵氏 A,24℃ Shaw A, 24 ℃ 2 |
80 | ASTM D2240 | |
邵氏 A,24℃ Shaw A, 24 ℃ 3 |
75 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变,24℃ 100% strain, 24 ℃ 2 |
2.76 | MPa | ASTM D412 |
100% 应变,24℃ 100% strain, 24 ℃ 3 |
MPa | ASTM D412 | |
100% 应变,100℃ 100% strain, 100 ℃ |
MPa | ASTM D412 | |
300% 应变,24℃ 300% strain, 24 ℃ 2 |
MPa | ASTM D412 | |
300% 应变,24℃ 300% strain, 24 ℃ 3 |
MPa | ASTM D412 | |
300% 应变,100℃ 300% strain, 100 ℃ |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
24℃ 24℃ 2 |
MPa | ASTM D412 | |
24℃ 24℃ 3 |
MPa | ASTM D412 | |
100℃ 100℃ |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂,100℃ Fracture, 100 ℃ |
% | ASTM D412 | |
断裂,24℃ Fracture, 24 ℃ 2 |
% | ASTM D412 | |
断裂,24℃ Fracture, 24 ℃ 3 |
% | ASTM D412 | |
撕裂强度 tear strength |
ASTM D470 | ||
开裂 cracking 4 |
kN/m | ASTM D470 | |
开裂 cracking 3 |
kN/m | ASTM D470 | |
开裂 cracking 2 |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积变化 Volume change |
ASTM D471 | ||
50℃,168 hr 50℃,168 hr 5 |
% | ASTM D471 | |
50℃,168 hr,ASTM 标准油(3号) 50 ℃, 168 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
50℃,168 hr,在基准燃料B中 50 ℃, 168 hr, in reference fuel B |
% | ASTM D471 | |
50℃,168 hr,在甲乙酮中 50 ℃, 168 hr, in methyl ethyl ketone |
% | ASTM D471 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
|||
100 ℃ 100 ℃ |
min | ||
脱模时间 stripping time |
|||
100℃ 100℃ |
min | ||
后固化时间 Post curing time |
|||
24℃ 24℃ |
hr | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
NBS NBS |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
100℃ 100℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 100% R.H. |
3 60% R.H. |
4 100°C |
5 in Toluene |
【新闻资讯】查看全部
每天几乎24小时不停工,福特启用移动机器人操作3D打印机
2022-03-18 在福特的先进制造中心,机器人Javier 可自行操作3D打印机他从不迟到,动作非常精准,每天大部分时间都在工作只需短暂的休息来充电。机器人Javier是由KUKA研发制造的自动移动机器人, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |